High Alumina Refractory Brick High Efficiency Durable Rotary Kiln Accessories
Brand Name:ZTIC
Certification:ISO\CE
Model Number:Fire brick
Minimum Order Quantity:≥1 Tons
Payment Terms:L/C, T/T
Place of Origin:Henan China
Contact Now
Add to Cart
Verified Supplier
Location:
Luoyang Henan China
Address:
No.2-A-609, NO.1 Longyu Road, Jianxi District, Luoyang, Henan, China
Supplier`s last login times:
within 13 hours
Product Details
Company Profile
Product Details
Product presentation
The mineral composition of high-alumina refractory bricks is corundum, mullite and glass phase, and its content depends on the ratio of AL2O3/SiO2 and the type and amount of impurities. The grade of refractory bricks can be divided according to the content of AL2O3. The raw materials are natural ores of high-alumina bauxite and sillimanite, and there are also those mixed with fused corundum, sintered alumina, synthetic mullite, and clinker calcined with alumina and clay in different proportions. It is mostly produced by sintering method. But the products also include fused cast bricks, fused granular bricks, unfired bricks and amorphous refractory bricks. High-alumina refractory bricks are widely used in the steel industry, non-ferrous metal industry and other industries.
Physical and chemical properties
1. Wear resistance:
2. Thermal conductivity: The heat flow rate per unit area of the
material under unit temperature gradient conditions, which is
related to the porosity
3. Impact resistance: No need to explain, good impact resistance
means long service life
4. Slag resistance: The ability to resist slag erosion without
being destroyed at high temperatures
Product features
One of the important working properties of high alumina refractory bricks is the structural strength at high temperature, which is usually evaluated by the load softening deformation temperature. Its high temperature creep is also measured to reflect its high temperature structural strength. The test results show that the load softening temperature increases with the increase of Al2O3 content.
The public properties of refractory raw materials mainly depend on the mineral composition and particle composition of the raw materials, and are closely related to the manufacturing process of refractory materials. Such properties mainly include particle size and particle size distribution, fineness and specific surface area, plasticity and bonding, drying shrinkage and firing shrinkage, sintering temperature and sintering range, etc.
Why choose us
1. High reputation, good product quality, worry-free after-sales,
honest production, no deception.
2. We have high-tech technical support, professional researchers to
develop, concentrate on manufacturing high-aluminum refractory
bricks, ensure product quality, and provide customers with better
quality and cheaper products.
3. We have a complete product production line and a scientific
management system to ensure product output quality and reassure
customers.
Product display
Product Parameter
| SK series | SK30 | SK32 | SK34 | SK35 |
| Al2O3 | 30%-35% | 35%-38% | 38%-42% | 42%-50% |
| Item | 33% Al2O3 | 38% Al2O3 | 42% Al2O3 | 48% Al2O3 |
| fire clay brick | fire clay brick | fire clay brick | fire clay brick | |
| Al2O3 | 33% | 38% | 42% | 48% |
| Fe2O3/% | ≤3 | ≤3 | ≤3 | ≤2.5 |
| Refractoriness | ≥1690 °C | ≥1730 °C | ≥1750 °C | ≥1750 °C |
| Bulk density/g/cm3 | 1.9-2.0 | 2.0-2.1 | 2.1-2.18 | 2.15-2.3 |
| Unit weight (230*114*65mm) | ≥3.35KGS | ≥3.55KGS | 3.65KGS | ≥3.75KGS |
| Apparent porosity/% | ≤26 | ≤24 | ≤24 | ≤22 |
| Cold crushing strength | ≥20Mpa | ≥25Mpa | ≥30Mpa | ≥35Mpa |
| Refractoriness under load | ≥1250 °C | ≥1300 °C | ≥1350 °C | ≥1420 °C |
| Reheating Linear Change/% | 0~ -0.5 | 0~ -0.3 | 0~ -0.4 | +0.1~ -0.4 |
| (1350°C,2h) | (1350°C,2h) | (1450°C,2h) | (1450°C,2h) |
Q&A
Q: Why we believe in luoyang zhongtai industries co., ltd:
A: 1. More than 30 years experience.
2.We are the leading professional supplier of mining machinery,
construction machinery, machines casting and forged parts.
3. All products achieved ISO9901:2000 quality management
certificate and CE, ROHS certificates.
Q:Delivery time?
A: Parts lead time 1-2months, machines 2-3months.
Q:Payment terms?
A: Accept payment type: T/T, L/C, Western union,Cash.
30% deposit when signed contract. Full payment paid before shipping
Q: Quality warranty?
A: Guarantee time: one year for main machinery. If something wrong
we will provide the technical advice and find solution immediately.
For those wearing parts we guarantee high quality parts for
long-term supply.
Q: After sales service?
A: We can supply technical guide for machines running test and
parts maintenance if end user needs.
High Alumina Refractory Brick High Efficiency Durable Rotary Kiln Accessories
Inquiry Cart
0