SiO2 Hydraulic Press Silica Refractory Bricks Erosion Resistance
Brand Name:ANNEC
Certification:ISO, CE
Model Number:YHRS
Minimum Order Quantity:200 pcs
Delivery Time:5-8 working days
Payment Terms:L/C, D/P
Contact Now
Add to Cart
Verified Supplier
Address:
Industrial Cluster Area of Xinmi City, Henan Province，China.
Supplier`s last login times:
within 23 hours
Product Details
Company Profile
Product Details
Introduction:
sizes and shapes for Silica Refractory Bricks are made with raw material high grade bauxite and SiC and special sintering process. Silica-mullite bricks are characterized by high density, good performance of abrasion resistance and thermal shock resistance. sizes and shapes for Silica Refractory Bricks can constantly form protective layer for reducing accrection formation, long application cycle,etc.
sizes and shapes for Silica Refractory Bricks Generally suitable for thermal surface refractory lining or other
refractory back lining insulation layer. Refractory lining or thermal insulation for industrial furnaces in
petroleum or chemical industries, such as ethylene cracking
furnaces, tubular furnaces, reforming furnaces for synthetic
ammonia, gas generators and high temperature shuttle kilns.
Tunnel kiln, push board kiln, roller kiln, wood kiln refractory lining material for industrial and household ceramics
sizes and shapes for Silica Refractory Bricks is made of silicon as raw material with high temp firing ,which silicon oxide is above 93% ,used in hot blast furnace,coke oven,glass kiln,these brick have good volume stability at high temperature, high refractoriness under the load,small rate of shrinkage in working condition.
Package:
sizes and shapes for Silica Refractory Bricks are packed on wooden pallet and then polyethylene film is placed
over it,finally the package is tied up with steel strips or as your
request
Good Acid Erosion Resistance Silica Checker Brick:
Item | Silica Brick for Coke Oven | Silica Brick for hot-blast Stove |
Brand | NCSB-94 | NCSB-95 |
SiO2 % ≥ | 94.5 | 95.0 |
Al2O3 % ≤ | 1.5 | 1.0 |
Fe2O3 % ≤ | 1.5 | 1.3 |
CaO % ≤ | 2.5 | -- |
Na2O+K2O% ≤ | -- | -- |
True Density≤ g/cm3 | 2.33 | 2.32 |
Apparent.Porosity.% ≤ | 23 | 22 |
Cold.Crushing.Strength(Mpa)≥ | 40 | 45 |
Permanent Linear Change%≤ | 0~-0.2 | 0~-0.2 |
Refractoriness Under Load 0.2Mpa | 1650 | 1650 |
Thermal Expansion Rate | 1.28 | 1.25 |
Competitive Advantage:
1. Good thermal shock stability,
2. High temperature mechanical strength;
3. High softening temperature under load,
4. Good slag resistance and alkali salt resistance
Zhengzhou Annec CO., Ltd. was founded in 2003, and has been a NASDAQ listed corporation since 2011 with ticker identification ANNC. Annec had become the industrial leader within China in the areas of refractory production, Engineering for hot blast stove of blast furnace, and capability for EPC project. Annec has its own Provincial Enterprise Technology Center and Top Combustion Hot Blast Stove Research Centre, Annec (Beijing) Engineering & Technology Co., Ltd and four Manufacturers for Refractories. The annual output of different type of refractories can reach 150 thousand tons, and undertaken capability of more than 10 turnkey projects for hot blast stove.
SiO2 Hydraulic Press Silica Refractory Bricks Erosion Resistance