Electro-Fused AZS Ramming Mass For Glass Melting Furnace Zirconium refractory Ramming Mass
Electro-fused AZS Ramming Mass
Electro-fused AZS refractory ramming mass is monolithic
refractories and electro-fused AZS refractory ramming mix is
composed of molten corundum aggregate particles and a small amount
of additives. Electro-fused AZS refractory ramming mass is prepared
by using high-quality zirconium aggregate, powder material,
aluminum phosphate as binder and admixture, which has low thermal
conductivity, good thermal shock resistance, chemical stability and
melting.
Glass and liquid metal have good corrosion resistance, work stability under oxidizing atmosphere, and do not chemically react with molten metal. Electro-fused AZS ramming material is an excellent thermosetting amorphous refractory material.
| Items | Fused AZS ramming mass |
| ZrO2% | 28 |
| Bulk density g/cm3 | 2.9 |
| Normal temperature compressive strength MPa 110℃drying ≥ | 50 |
| Refractoriness/ | 1770 |
| Maximum Service temperature/℃ | 1650 |
| Use density kg/m3 | 3000 |
Advantages of Electro-fused AZS Ramming Mass:
convenient for use
small thermal expansion and shrinkage
strong resistance to solution corrosion.
hardening at normal temperature, high compressive strength in high
temperature
Applications of Electro-fused AZS Ramming Mass:
Sealing layer of glass and frit bath kiln.
Used in the field of glass furnace kiln, ladle and circulating
fluidized bedboiler.