EN 1.4418 Hot Rolled Forged Alloy Round Bar Bright Bar Alloy 1.4418 Shaft
Brand Name:DELTA
Certification:ISO
Model Number:1.4418
Minimum Order Quantity:500 kgs
Delivery Time:5 - 12 days based on the quantity
Payment Terms:L/C, T/T, Western Union
Contact Now
Add to Cart
Verified Supplier
Location:
Wuxi Jiangsu China
Address:
No.283-1, Youyi Middle Road, Xishan District, Wuxi City, Jiangsu Province
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
EN 1.4418 Hot Rolled & Forged Alloy Round Bar Bright Bar Alloy 1.4418 Shaft
| Form | Nickel Alloy Bars |
| Grade | 1.4418 |
| Outer Diameter | 6mm-300mm or according to customer’s requirement |
| Length | custom cutting any length as request |
| Standard | ASTM, ASME, EN, JIS, DIN, GB/T, etc |
| Process Method | Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar & Rod |
| Surface Finish | Bright, Hot Rolled Pickled, Cold Drawn, Sand Blasting Finished, Polished, Hairline |
| Other Grade | Hastelloy : B2 B3 C22 C276 G30 X |
| Price Item | EXW FOB CFR CIF |
| Payment | 30% TT inadvance, 70% TT Balance against copy of B/L |
| Delivery Time | It depends on your bars order total quantity and stock of these mother origin materials. Usually from the start of the order to the completion of production is about 3-4 weeks |
| Quality Requirement | Mill test certificate will be offered with shipment, the third party inspection is available |
| Main Markets | Europe, North America, Middle East, Southeast Asia |
| Metal Test | High or low temperature impact test, metallographic analysis |
| Chemical Analysis | As nickel alloy 718 bars standard |
About 1.4418 Alloy
1.4418 stainless steel is a high-strength, low-carbon martensitic stainless steel. Its composition consists of 80% Martensite, 10% Austenite & 10% Ferrite, allowing for a low-carbon structure after quenching & tempering.
Supplied Condition (where applicable):
- We supply 1.4418 quenched (hardened) & tempered to QT900
- Specifications: EN 10088-3
Chemical Composition of Alloy 1.4418
- Carbon (Maximum)0.06
- Phosphorus (Maximum)0.04
- Silicon (Maximum)0.7
- Nickel (Nominal)5
- Manganese (Maximum)1.5
- Sulfur (Maximum)0.03
- Chromium (Nominal)16
- Molybdenum (Nominal)1.2
- Iron (Nominal)Balance
- Nitrogen (Nominal)0.02
Properties of 1.4418 Alloy
- Combine high tensile strength, excellent fatigue resistance & good weldability - high toughness is maintained even after welding
- Are designed for slightly corrosive environments, better corrosion properties than most stainless martensitics
- Poor weldability
- Magnetic
Mechanical Properties (Specific for Bars – Condition QT900)
| Dimensions (mm) | Yield strength Rp0.2, MPa | Tensile strength Rm, MPa | Elongation [%] | Hardness [HB] | Impact, Charpy-V, 20ºC [J] | Impact, Charpy-V, -40ºC [J] |
| < 160 | ≥ 700 | 900 – 1100 | ≥ 16 | 280 – 340 | ≥ 80 | ≥ 32 |
| 160-250 | ≥ 700 | 900 – 1100 | ≥ 14 | 280 – 340 | ≥ 60 | ≥ 32 |
Application of 1.4418 Alloy
- Water turbine parts
- Propeller shafts
- Piston rods
- Hydro power station equipment
- Spindles
- Bolts
- Shear pins
EN 1.4418 Hot Rolled Forged Alloy Round Bar Bright Bar Alloy 1.4418 Shaft