Hot Rolled C Section Steel Channel Strong Framework Strut Simple Plain Design

Steel st20, C22E, C22R, 1.1151, 1.1149 - specification and application

Grade 20 is a simple structural carbon steel used in the production of low-load machine parts and structures with good weldability, not requiring high strength properties in a heat-treated state.

In the annealed state, the steel is characterized by good machinability, while in the normalized state, the material shows a much better susceptibility to mechanical cutting.

C22E / C22R steel is supplied mainly in the form of round bars, is intended for connecting rods, connectors, shafts, overhead cranes, bolts, pins, bushings, control shafts, axles, keys, rivets, wedges and hubs.

General mechanical properties of C22E, 1.1151, C22R, 1.1149 steel according to EN 10083-2

• Normalized condition +N
• Tensile strength, Rm: >410 MPa
• The yield point, Re: > 210 MPa
• Elongation, A:> 24%
• Heat-treated condition +QT
• Tensile strength, Rm: 470 - 650 MPa
• The yield point, Re: > 290 MPa
• Elongation, A:> 20%
• Contraction, Z: >50%
• Impact resistance, KV: > 50J

Mechanical properties of cold rolled strips C22E, 1.1151, C22R, 1.1149 according to EN 10132-3

1. Annealed condition +A+LC
2. Tensile strength, Rm: <500 MPa
3. The yield point, Re: <400 MPa
4. Elongation, A: <22%
5. Hardness, HV: < 155
6. Hardness, HRB: <78
7. Delivery condition +CR
8. Tensile strength, Rm: <900 MPa
9. Hardness, HV: < 265

Heat and plastic treatment

• Forging at 1100 - 850 ℃
• Rolling at a temperature of 1180 - 850 ℃
• Softening annealing at a temperature of 650 - 700 ℃
• Normalizing annealing at temperatures of 850 - 920℃
• Hardening at 860 - 900℃ with cooling in water
• Tempering at a tempering of 550 - 660℃