65mn 1066 Spring Steel Coil , Spring Steel Strip Tempered Treated 0.8-8mm Thick
Brand Name:JIN LAI
Certification:ISO
Model Number:65MN
Minimum Order Quantity:3 tons
Delivery Time:within 15 days
Payment Terms:T/T, Western Union, L/C
Contact Now
Add to Cart
Active Member
Location:
Wuxi Jiangsu China
Address:
NO.21 Dongting Road,Xishan District,Wuxi ,Jiangsu,China
Supplier`s last login times:
within 41 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
65MN Chemical composition
| C(％) | 0.62-0.70 | Si(％) | 0.17-0.37 | Mn(％) | 0.90-1.20 | P(％) | ≤0.035 |
| S(％) | ≤0.035 | Cr(%) | 0.25max | Ni(%) | 0.25max |
Equivalent Of 65Mn alloy Spring Steel
| USA | Germany | China | Japan | France | England | Italy | Poland | ISO | Austria | Sweden | Spain |
| AISI/SAE/ASTM/UNS | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | ISO | ONORM | SS | UNE |
| 1066 | 65Mn | 080A67 | |||||||||
Heat treatment Related
- Annealing of 65Mn Spring Steel
At first Slowly heated to 730 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. Then 65Mn tool steel will get MAX 250 HB (Brinell hardness).
- Hardening of 65Mn Spring Steel
At the beginning, 65Mn steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. After about 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil. Tempering of 65Mn Spring Steel
Tempering of 65Mn steels is performed at 540°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Hardness values at different temperatures after tempering
Mechanical Properties
The mechanical properties of 65Mn Spring Steels are outlined in the following table.
| Tensile strength | Conditions to yield strength | Elongation | Reduction of area | Hardness (Hot Rolled) | Hardness (Cold Drawn) |
| σb (MPa):≥980 | σ0.2 (MPa):≥785 | δ 5 (%):≥8 | ψ (%):≥30 | ≤302HB; | |
Applications
65Mn steel, after heat treatment and cold drawing hardening, high strength, it has a certain toughness and plasticity; In the same surface hardening case, completely and the fatigue limit and alloy spring. But hardenability poor, mainly for the smaller size of the spring, such as regulating speed regulating spring, spring load, general machinery in the round, square spiral spring or pull wire for small mechanical spring.
Regular size and Tolerance
Steel round bar: Diameter Ø 2mm – 3000mm
Steel plate: Thickness 2mm – 3000mm x Width 100mm – 3500mm
Steel Hexagonal bar: Hex 5mm – 105mm
Others 65Mn have not specified size, pls contact our experienced sales team.
Processing
Moreover, GB 65Mn Spring Steel round bar and flat sections can be cut to your required sizes. 65Mn Spring Steel ground bar can also be supplied by us, providing a high quality Spring Steel precision ground Spring Steel bar to your required tolerances. And GB 65Mn steel is also available as Ground Flat Stock / Gauge Plate, in standard and nonstandard sizes.
65mn 1066 Spring Steel Coil , Spring Steel Strip Tempered Treated 0.8-8mm Thick