HRC 60 Powdered Metal Gears Density 6.5g/Cm3 For Automotive Subassemblies
Brand Name:SFT
Minimum Order Quantity:negotiable
Delivery Time:20-45DAYS
Payment Terms:L/C, T/T, Western Union, MoneyGram
Place of Origin:China
Price:negotiable
Contact Now
Add to Cart
Verified Supplier
Address:
A-709 Zhengshang International Building, Fengcheng 8 Road,Xi'an,China
Supplier`s last login times:
within 19 hours
Product Details
Company Profile
Product Details
Powder metal products for small gears and miniature components
powder metal products for small applications, including small gears and miniature components for planetary drives, automotive sub-assemblies, drills, and electronics, and in particular, small components and assemblies for medical devices.
Specialists in stainless steel and material blending, SFT provides
you with technical expertise and the ability to discover a cost
effective solution that maintains the integrity of your design.
The benefits of powder metal products include:
- High Quality, High Strength Small Metal Parts to Precision Tolerances.
- Up to 70% Cost Savings over Other Processes.
- Repetitive Accuracy.
- Dimensional Accuracy.
- Ability to Tailor Material to Be Ductile or Hard.
- Ability to Blend Materials to Gain Desirable Properties.
- Corrosion Resistance.
- Scrap-Free, Environmentally “Green” Manufacturing Process.
Performance of Oil Bearing
| (1)Performance of oil bearing (copper based & iron based) | |||||
| No. | Features | ||||
| Illustrate | Unit | Copper based | Copper & iron based | Iron based | |
| 1 | Density | g/cm3 | 6.5-7.2 | 6.0-6.7 | 5.9-6.5 |
| 2 | Surface porosity | / | After heated in lubricating oil from the sliding surface | ||
| 3 | Noise (distance 50 mm) | db | below 20 | ||
| 4 | Abrasion loss | m | below 15 | ||
| 5 | Oil Content Rate | V% | above 18 | ||
| 6 | Pressure stains strength | Mpa | above 150 | above 250 | above 280 |
| 7 | Hardness | MHV | 60-90 | 60-90 | 60-110 |
| 8 | Friction coefficient | / | below 0.15 | below 0.25 | below 0.25 |
| 9 | Life | h | above 2000 | ||
| (2) Performance of structuralparts (copper based & iron based) | ||||||||||
| No. | Cu | Ni | Mo | C | Fe | Density g/cm3 | Tensile strength Mpa | Elongation % | Hardness HB | Perfect for |
| 1 | ＜1 | / | / | ＜0.3 | other | 6.4-6.8 | 150 | 4 | ＞45 | Low load structure |
| 2 | 1-5 | / | / | ＜0.3 | other | 6.4-6.8 | 200 | 3 | ＞55 | Middle load structure |
| 3 | 1-5 | / | / | ＜0.3 | other | 6.8-7.2 | 300 | 7 | ＞80 | High load structure, can carburizing heat treatment |
| 4 | 1-3 | 1-5 | ＜0.8 | 0.3-0.6 | other | 6.8-7.2 | 600 | 2 | ＞160 | Upper load structure, can heat treatment |
| 5 | 3-5 | 1-5 | ＜0.8 | 0.3-0.6 | other | 7.2-7.4 | 700 | 2 | ＞180 | Higher load structure, can heat treatment |
Dimensions and Capacities
| Type | Max.Torque (N.m) | Nominal Overrunning Drag(N.m) | Max. Overrunning (r/min) | Max. Indexing (cycle/min) | Stock Bore Size | ||
| Inner Race | Outer Race | Dia (H7) | Keyway | ||||
| MZ15 | 186 | 0.20 | 1800 | 900 | 150 | 15 | 5×2.3 |
| MZ17 | 215 | 0.20 | 1700 | 800 | 150 | 17 | 5×2.3 |
| MZ20 | 323 | 0.29 | 1600 | 700 | 150 | 20 | 6×2.8 |
| MZ30-22 | 735 | 0.39 | 1500 | 500 | 150 | 22 | 6×2.8 |
| MA30-25 | 25 | 8×3.3 | |||||
| MZ30 | 30 | 10×3.3 | |||||
| MZ35 | 1080 | 0.49 | 1400 | 300 | 150 | 35 | 10×3.3 |
| MZ45-40 | 1620 | 0.69 | 1400 | 300 | 150 | 40 | 12×3.3 |
| MZ45 | 45 | 14×3.8 | |||||
| MZ60-50 | 2110 | 0.98 | 1200 | 250 | 150 | 50 | 14×3.8 |
| MZ60-55 | 55 | 16×4.3 | |||||
| MZ60 | 60 | 18×4.4 | |||||
| MA70-65 | 3040 | 1.27 | 1100 | 250 | 150 | 65 | 18×4.4 |
| MA70 | 70 | 20×4.9 | |||||
HRC 60 Powdered Metal Gears Density 6.5g/Cm3 For Automotive Subassemblies