Brass Electroplating Production Line Brass Electroplating Machine
1. Main parameters of electroplated brass production line.
No | Item | Specification |
1 | material | steel wire |
2 | wire diameter range | φ0.45~φ3.5 mm |
3 | coating type | brass |
4 | content of copper | 62~68% |
5 | coating weight | 3~8g/kg |
6 | wire lines | 36,48 or 56 lines |
7 | speed(DV) | DV=75 or 95m*mm/min(max speed 70 or 90m/min) |
8 | fuel type | NG or LPG |
2. Technological process of production.
pay off→degreasing→heat treatment→patenting→water
cooling→pickling→water rinsing→copper plating→water rinsing→zinc
plating→water rinsing→hot water rinsing→MF→phosphoric acid
wash→water rinsing→soaping→take up
3. Main process introduction.
Degreasing: remove the uneven soap powder and borax, and paint a layer of
soap powder and borax on the surface of bright steel wire, so that
the surface coating of steel wire is more uniform.
Heat treatment: make the deformation hardening steel wire to restore the
ductility, and obtain the ideal microstructure to meet the cost of
steel wire in tensile strength, shape, elongation and other
requirements.
Patenting: the heat-treated steel wire is cooled down from high temperature,
and the water vapor quenching process is used to obtain strong
strength and shaped sostenitic structure.
Pickling: remove all oxides and residues on the surface of the steel wire,
and the clean surface is conducive to uniform coverage of the rear
coating.
Copper plating: a layer of copper is uniformly plated on the surface of the steel
wire, so that the subsequent brass is conducive to drawing.
Zinc plating: deposition of metal zinc on the surface of steel wire.
MF: the method of intermediate frequency heating makes the copper and
zinc layers of steel wire diffused with each other to get brass.
The effect of intermediate frequency annealing is to raise the
surface of the steel wire to a certain temperature to make the zinc
and copper mutually diffused.
Phosphoric acid wash: remove the zinc oxide produced on the surface of the steel wire
in the intermediate frequency thermal diffusion stage, which is
hard and not easy to deform. Too much zinc oxide will lead to
broken wire in the wet drawing process.
4.Product application
tire meridian, cutting steel wire, diamond busbar, hose wire, etc.
5. Our Services
In order to guarantee the customers are able fully to operate the
machine, if the customer need, we can help customer training,
includes:
(1) Correct operating mode
(2) Correct maintenance way
(3) Correct technological process control
(4) Remove simple problem
All the electroplating machine of our company have already been
widely used in electroplating area.