Product Details
[Carbon Steel] ER50-Ti ER70S-G Used For LCS With Strengthened
Current 0.8mm 1.0mm 1.2mm 1.6mm
ER50-Ti ER70S-G Hot Rolled Low Carbon Iron 5.5mm Steel Wire
Conform to Standard
GB/T 8110 ER50-G
ISO 14341-B-GS11
AWS ER70S-G
JIS YGW11
Specification:The welding current has been strengthened to a great extent and the
welding efficiency has been improved. Because the grains of the
deposited metal have been refined, both the tensile strength and
the yield strength will be improved too.
Slag-forming gas shielded flux-cored wire | CO2 gas shielded flux-cored welding wire, the main varieties are used for carbon steel, 50 kg low alloy structural steel (all-position welding), high strength steel, low temperature steel, heat-resistant steel (1.25Cr-0.5Mo series, 2.25Cr-1Mo series), weathering steel (painted and non-painted), stainless steel (welded SUS304, 304L, 316, 316L, 317, 317L, 321, 347, 309S
stainless steel), wear-resistant surfacing (Hv250, Hv350, Hv450, Hv600). |
Ar-rich mixed gas shielded flux-cored welding wire, mainly used for carbon steel, 50kg low-alloy structural steel (all-position welding), high-strength steel (60-70kg), low temperature steel (-45°C, -60°C impact toughness), wear-resistant surfacing (13Cr-2Ni series). |
Metal powder cored flux cored wire | CO2 gas shielded flux-cored welding wire, the main varieties are used
for carbon steel, 50kg low alloy structural steel, high strength steel (60kg), wear-resistant surfacing (high Cr-Fe series, Hv800) |
Ar-rich mixed gas shielded flux-cored welding wire, mainly used for carbon steel, 50kg low alloy structural steel, low temperature steel (-60℃ impact toughness), stainless steel (13Cr-5Ni series, 13Cr-4Ni-Mo series, 17Cr series), wear-resistant surfacing (13Mn series, 16Mn-16Cr series). |
Chemical Composition(%)
Chemical Composition | C | Mn | Si | S | P | Ti+Zr | Cu |
Guarantee Value | ≤0.15 | 1.40~ | 0.55~ | ≤0.030 | ≤0.030 | ≤0.30 | ≤0.50 |
1.9 | 1.1 |
General Result | 0.061 | 1.44 | 0.73 | 0.012 | 0.009 | 0.16 | 0.124 |
Mechanical Properties of Deposited Metal
Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) |
-30℃ |
Guarantee Value | ≥500 | ≥420 | ≥22 | ≥27 |
General Result | 545 | 455 | 29 | 114/131/127 |
Reference Current(DC+)
Size(mm) | Current range (A) | GAS flow rate(L/min) |
Φ0.8 | 50~100 | 15 |
Φ1.0 | 50~220 | 15~20 |
Φ1.2 | 80~350 | 15~25 |
Φ1.6 | 170~550 | 20~25 |
Company Profile
Established in 1993 as a township enterprise
Cover an area of over 3 million square meters with staff of more
than 5500.
Vice President Company of CANSI
(China Association of National Shipbuilding Industry)
Six main products series (4.3 million tons)
1. Welding Materials
2. Shipbuilding section
3. High-strength pre-stressed concrete steel bar
4. Forging ingot series
5. Steel ball series for bearing & mining industry
6. Flange & End Plate
As our develop strategy, we have been focusing on the complete
production process mode which we deem will bring us synergy, so
recently, another new product, i.e. welding consumables will be
added to our catalog which will cover all series such as
gas-shielded solid welding wire、flux cored wire、submerged arc
wire、argon arc wire etc.
We have two main advantages for LT welding wires:
Fully integrated production process, i.e., with the support of
upstream world class steel making facilities in house from same
group company.
Newly developed production process with latest technology and
know-how, i.e., fully automatic production which will be the
assurance of quality control.