product name: refractory high aluminum brick grade 1
product description:
Characteristics of high alumina brick
1, fire resistance
The fire resistance of high alumina bricks is higher than that of
clay bricks and semi-silicon bricks, reaching 1750 ~ 1790 °C, which
is an advanced refractory material.
2 , Load softening temperature
The load softening temperature of high alumina brick is 1420 ~ 1520
° C. The content of AL2O3 increases and the charge soft temperature
increases. Because of the high content of Al2O3 in high alumina
bricks, less impurity quality, the formation of less fusible glass
phase, so the load softening temperature is higher.
3, slag resistance
The high alumina brick has more Al2O3, which is close to the
neutral refractory material, and can resist the erosion of acid
slag and alkaline slag. Because it contains SiO2, the ability to
resist alkaline slag is weaker than that of acid slag. The content
of AL2O3 increases, the impurities decrease, and the slag
resistance increases.
Application field of high alumina brick
1.Steel manufacturing : blast furnace, hot stove, electric furnace,
ladle, tundish, heating furnace, refining furnace, heating furnace,
annealing furnace, cupola ;
2, non-ferrous metal industry : smelting furnace, refining furnace,
reflecting furnace, converter ;
3, building materials industry : cement kiln, glass kiln, ceramic
kiln, lime kiln, kiln car, tunnel kiln ;
4. Energy and incineration : coke oven, circulating fluidized bed
boiler, carbon baking furnace, incinerator.
product index:
Item | First grade high alumina brick | Secondary high alumina brick | Three grade high alumina brick | special high alumina brick |
AL2O3 %≥ | 75 | 65 | 55 | 82 |
Fe2o3 %< | 2.5 | 2.5 | 2.6 | 2 |
volume density g/cm3 | 2.5 | 2.4 | 2.3 | 2.6 |
cold crushing strength MPa> | 70 | 60 | 50 | 80 |
load softening temperature ℃ | 1510 | 1460 | 1420 | 1550 |
refractoriness ℃> | 1790 | 1770 | 1770 | 1790 |
apparent porosity % | 22 | 23 | 24 | 21 |
linear change rate % | -0.3 | -0.4 | -0.4 | -0.2 |