Prevent Adhesion and Agglomeration with Powder Coating Additives for Metal Bonding Process

Metal Bonding Additives Powder Coating Additives Prevent Adhesion and Agglomeration, Improve Mirror Effect

Product:Metal bonding agent

Model:HD-816

Composition:Micropowder modified polymer homopolymer

Technical Parameter :

Function:

Addition amount and usage method:

1.The addition amount of metal bonding additives for HD-816 is generally 0.2-1.5%

2.Using heating bonding equipment, add HD-816 and the base powder together into a hot mixing cylinder, stir and raise the temperature to about 65 ℃. Slowly stir and add metal pigment powder, control the temperature for 10-25 minutes. Place the material in a cold mixing cylinder, stir slowly, and quickly cool the powder to below 35 ℃. Add flow additives, and place the material through a sieve.

Product packaging: 15kg/pack 20kg/pack (lined with polyethylene bag)

Storage:It should be stored in a clean, ventilated, and dry warehouse to avoid impurities mixing in

Notes:The conditions and ratios listed in this manual are for reference only. It is recommended that users make appropriate adjustments based on specific equipment, materials, environment, and application conditions before use.

Dongguan Yangting New Material Technology Co., Ltd. specializes in the production and sales of various types of wax powder. The main products are polyethylene wax, polypropylene wax, polyamide wax, oxidized polyethylene wax. Ptfe wax powder, etc., can be widely used in paint/ink industry/powder coating, etc., and also used in the manufacture of color masterbatch, PVC pipe, hot melt adhesive, rubber whitening agent, cable insulation material, floor wax, plastic, ink, injection molding products, etc