95% Al2O3 Balls Alumina Oxide Balls Acid And Alkali Resistant
Brand Name:HUAO
Certification:ISO9001 ISO14001 ISO45001
Model Number:OEM
Alumina Content:92%,95%,99%
Hardness:9
Size:Can be customized design
Contact Now
Add to Cart
Verified Supplier
Location:
Zibo Shandong China
Address:
NO.1208, LIUQUAN ROAD, HIGH TECH AREA, ZIBO, SHANDONG, CHINA, 255000
Supplier`s last login times:
within 22 hours
Product Details
Company Profile
Product Details
95% Al2O3 Balls
Product discription
95% Al2O3 Balls are made from good quality and high temperature alumina powder. It is used for polishing of metal parts and grinding for non-metallic mineral powder(for instance zirconium silicate, kaolin and so on). It applies to all types of grinding and polishing machine. It is the grinding media for ball mill, pot mill, vibration mill and other fine powder grinding equipment, its grinding and wear resistance efficiency is much better than normal balls and nature stones. They have characters of high purity, high strength, high hardness, more white, low abrasion, high temperature resistance, acid and alkali resistance, corrosion resistance.
Advantages
95% Al2O3 Balls are wigely used in petroleum, chemical, fertilizer, natural gas and environmental protection industries. They are used as covering support materials for catalysts in reactors and tower packing.
Parameter list
| Materials | Density (g/cm³) | Bulk weight (g/cm³) | Moh's hardnesss | Crushing rate | Abrasion loss |
| Alumina grinding media | 3.6-3.8 | 2200-2300 | 9 | ＜1-3 | 0.09 |
| High chromium steel ball | 7.6-7.8 | 4500 | 6.8 | ＜1-3 | 0.18 |
Application
95% Al2O3 Balls are grinding bodies used for fine grinding equipment such as ball mills, pot mills, vibratory mills and so on. It can be subdivided into two types: wet grinding and dry grinding.
FAQ
1.Payment term
30% TT Deposit for PO Confirmation, 70% TT before Delivery
2.Packing Detail
Carton, wooden, or according to customs' requirement.
Editor:Jiahui
95% Al2O3 Balls Alumina Oxide Balls Acid And Alkali Resistant
Inquiry Cart
0