0.2-3.5mm Zirconia Ceramic Beads /Ball Used As Grinding Media
Product Introduction
Zirconia used in calcium carbonate, kaolin, zircon sand, pigments,
dyes, graphite, coatings, metal mining industries used as grinding
and dispersion media. The beads can also be used for shoot peening
polishing and other metal surface treatment. According to the
customer's different grinding equipment, we can match different
density grinding beads.
Properties
Good roundness, high sphericity, the surface has excellent gloss.
the product is compact in sintering and has no defects such as
porosity and so on.
Excellent toughness, higher crushing strength than ordinary alumina
beads, non-fragmentation in long-term high speed operation.
Good stability, acid and alkali resistance.
Low equipment attrition.
Product Size
∅0.2-0.4mm | ∅0.4-0.6mm | ∅0.6-0.8mm | ∅0.8-1.0mm | ∅1.0-1.2mm |
∅1.2-1.4mm | ∅1.4-1.6mm | ∅1.5-2.0mm | ∅2.0-2.5mm | ∅2.5-3.0mm |
∅3.0-3.5mm | ∅4mm | ∅5mm | ∅8mm | ∅10mm |
Detail Sheet
ZTA280 | ZTA320 | ZTA370 | ZTA380 | ZTA450 | ZTA470 | |
Al2O3(%) | ≥57 | ≥70 | ≥87 | ≥66 | ≥5 | ≥3 |
ZrO2(%) | ≥5 | ≥5 | ≥5 | ≥18 | ≥62 | ≥70 |
SiO2(%) | ≤30 | ≤20 | ≤5 | ≤12 | ≤30 | ≤24 |
Bulk density(g/cm³) | ≥2.80 | ≥3.15 | ≥3.70 | ≥3.78 | ≥4.48 | ≥4.60 |
HV Hardness(Gpa) | ≥7 | ≥8 | ≥12.5 | ≥11 | ≥10 | ≥10 |
Crushing Strength(N) | ≥25 | ≥800 | ≥1000 | ≥12000 | ≥1200 | ≥1300 |
Water absorption | <0.01 | <0.01 | <0.01 | <0.01 | <0.01 | <0.01 |
Wear loss rate(g/kg.h) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Sphericity | ≥95% | ≥95% | ≥95% | ≥95% | ≥95% | ≥95% |