High Dilution Carbon Fiber Release Agent Water Based Mold Release For Composites
Brand Name:Lubekote
Model Number:xxxxx
Minimum Order Quantity:None
Delivery Time:5-15 working days
Payment Terms:T/T
Place of Origin:China
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
Floor 2-3, Building 20, Hongxing International Plaza, Lane 1818, Lianhang Road, Pujiang, Shanghai
Supplier`s last login times:
within 48 hours
Product Details
Company Profile
Product Details
High Dilution Water-Based Carbon Fiber Release Agent Lubekote 9405
Carbon fiber composite material is a very practical polymer material, from the initial aerospace applications to now slowly into people's lives, after continuous innovation and research and development in recent years, China's carbon fiber composite material whether material or performance has reached a very advanced level. First of all, carbon fiber composites are very strict and high hardness, but at the same time very lightweight. The composite structure of this second major component - resin - ensures that the prefabricated wire permanently maintains its preset shape.
The role of a suitable compound release agent is particularly important in the production process, which can better solve the smooth and smooth surface of the product in each release process. And Leorui inherent very suitable products applied to different process products, and let you in the release process of each release smooth, off the smart. Water-based products Lubekote 9405 is high dilution and environmental protection, suitable for most of the carbon fiber products release.
Advantages:
- Does not transfer to the product parts.
- Low odour
- No knit lines.
- Minimal build-up on mold
- Excellent surface
Application:
The mold should be thoroughly cleaned.
Mold cleaning and release agent application should be performed in
a well ventilated area.
1. Apply Lubekote release agent to clean, dry cotton cloth.
2. Gently wipe over mold surface covering an area of approximately
0,5 m². Vigorous rubbing or polishing is not required.
3. Repeat steps 1 and 2 on the adjacent area. Ensure a good overlap
with the previous area to provide complete coverage
4. Repeat until mold is completely coated.
5. When dry, allow a further 15 minutes between coats for the film
to cure.
6. Repeat Steps 1- 5 above for a further 3 coats (4 in total).
7. When dry, allow final film to cure for at least 30 minutes at
room temperature before molding. Allowing a longer cure or heat
curing (e.g. 15 min. at 60 °C) will improve film durability
Reapply one coat of Lubekote release agent in the same way as
described above when release becomes hesitant.
Handling precautions:
For industrial use only.
More release agent producst.
| Application | Product | Advantages |
| Bicycle frame | Lubekote 9511/9308 | volatile fast, release agent good less fouling, cost-effective |
| Racket/helmet | Lubekote 9072/9071 | semi-permanent, fast volatilization, good brightness, no fouling, post process |
| Snowboard/fishing rod | Lubekote 9129A/9125A | water-based easy to operate, mold rust, environmental protection, harmless to people |
Shanghai LoreChem Co., Ltd. was established in 2008. It is a
high-tech enterprise which is dedicated to serve releasing products
which involve semi-permanent release agent, anti-sticking, surface
lubrication and thermal reactive adhesive. Shanghai LoreChem has
been improving product quality for 15 years. The releasing products
are mainly applied in rubber, polyurethane and composite industry.
The brand of Lubekote for release agent and Thinkbond for adhesive
have been registered in China. Both of them are well known in the
industry.
Shanghai LoreChem 's business is all over the domestic and foreign
high-end production enterprises by providing professional technical
solutions and services. The company's long-term goal is to become
one of the best suppliers of release agent in Asia.
High Dilution Carbon Fiber Release Agent Water Based Mold Release For Composites
Inquiry Cart
0