Landfill and Environmental Protection HDPE Smooth Geomembrane with 2.0-3.0% Carbon Black Content and Flexible Durable Design
Brand Name:JianYi
Certification:ISO9001
Place of Origin:China
Carbon Black Content:2.0-3.0%
Application:Landfill, Mining, Pond Liner, etc.
Tear Resistance:93-374N
Contact Now
Add to Cart
Verified Supplier
Location:
Changsha Ningxia China
Address:
Chuangye Avenue,Ningxiang Economic Development Zone,Changsha City,Hunan Province,P.R.C.
Supplier`s last login times:
within 19 hours
Product Details
Company Profile
Product Details
Flexible and Durable HDPE Smooth Geomembrane for Landfill and
Environmental Protection
Product Introduction
Smooth surface geomembrane is an important building material,
belonging to one of the geosynthetics. It is mainly used in
engineering projects such as impervious, isolation and
reinforcement. It is made from high-density polyethylene (HDPE) as
the main raw material, with a certain amount of carbon black,
antioxidants, anti-aging agents, ultraviolet absorbers and color
masterbatches added through a special formula. It is then
mass-produced by a highly automated process using a three-layer
co-extrusion blow molding technology.
Product Properties
High tensile strength, high tear resistance, good flexural,
flexibility, elasticity, adapt to geological uneven settlement,
strong acid, alkali, oil corrosion resistance, excellent chemical
corrosion resistance, good heat resistance and cold resistance.
Product Application
Smooth geomembrane is widely used in water conservancy,
environmental protection, municipal engineering, aquaculture,
sewage treatment, tailings dam seepage control, landfill, landscape
gardening, and hydraulic engineering, etc. For example, in
hydraulic engineering, it can be used for the impervious leakage
prevention of reservoirs; in sewage treatment projects, it can
prevent sewage seepage.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | |||||||||
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Density (g/c㎡,≥) | 0.939 | ||||||||
| Tensile Properties | |||||||||
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yeild Elongation Rate (%) | 12 | ||||||||
| Breaking Elongation Rate (%) | 700 | ||||||||
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) | 300 | ||||||||
| Carbon Black | |||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | ||||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | ||||||||
| Oxidative Induction Time (OIT) | |||||||||
| Standard OIT (min) | 100 | ||||||||
| High Pressure OIT (min) | 400 | ||||||||
| 85℃ Oven Ageing (Minimum Average) | |||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | ||||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | ||||||||
| The Anti-UV Strength | |||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | ||||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | ||||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | ||||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | ||||||||
| Dimensional Stability | ±2 | ||||||||
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
| Specification Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark | |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | ||
| Density (g/c㎡,≥) | 0.94 | ||||||||||
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | ||
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | ||
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |||||||
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | ||||||||||
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | ||
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | ||
| Carbon Black Content (%) | 2.0~3.0 | ||||||||||
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed | ||||||||||
Landfill and Environmental Protection HDPE Smooth Geomembrane with 2.0-3.0% Carbon Black Content and Flexible Durable Design