Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250
Brand Name:LEOTECH
Certification:CE
Model Number:UT-ML
Minimum Order Quantity:500 pcs
Payment Terms:T/T
Place of Origin:Chongqing, China
Contact Now
Add to Cart
Verified Supplier
Location:
Chongqing Chongqing China
Address:
Room X1714, 3rd Floor, Building 4 No. 121, Yuzhou Road, Shiqiaopu Jiulongpo District Chongqing 400039 CHINA
Supplier`s last login times:
within 47 hours
Product Details
Company Profile
Product Details
Yttria-Stabilized Zirconia Blank 10.5×10⁻⁶/K Thermal Expansion
≤3-Unit Bridges HV10 1150-1250
UT-ML Dental Zirconia Block
● High Strength ● High Transparency ● Natural
UT-ML: Aesthetic & Durable Dental Zirconia
Achieve natural aesthetics with 49–53% translucency and multilayer effects. Exceptional strength (800 MPa) ensures longevity for crowns and 3-unit bridges. Biocompatible (0 cytotoxicity) and low radioactivity (<0.1 Bq/g). Monoclinic phase <5% post-aging guarantees stability.
Achieve natural aesthetics with 49–53% translucency and multilayer effects. Exceptional strength (800 MPa) ensures longevity for crowns and 3-unit bridges. Biocompatible (0 cytotoxicity) and low radioactivity (<0.1 Bq/g). Monoclinic phase <5% post-aging guarantees stability.
Product Parameters:
| Model | UT Multilayer 95mm |
| Size | 95mm |
| Strength | 600-800 MPa |
| Shades | 16 VITA Classical. |
| Disc Sizes | 9 thicknesses(10,12.14.16.18.20.22.25.30mm) |
Technical Parameters:
1.Chemical composition
| Components | UT-ML |
| ZrO2+HfO2+Y2O3 | ≥99% |
| Y2O3 | 8.0%-10.0% |
| Al2O3 | ＜0.15% |
| Other Oxides | ＜0.5% |
2.Physical characteristics
| Properties | UT-ML |
| Density before sintering(g.cm-3) | 3.15±0.05 |
| Density after sintering(g.cm-3) | 6.06±0.02 |
| CTE(25-500℃)(K-1) | (10.5±0.5)×10-6 |
| Flexural strength after sintering(Mpa) | 600-800 |
| Translucency(1.0±0.02mm) | 49%-53% |
| Fracture toughness(MPa.m1/2) | 3.5-5.0 |
| Hardness(HV10) | 1150-1250 |
| Accelerated aging surface monoclinic phase content | ＜5% |
| Chemical solubility after sintering(μg.cm-2) | ＜100 |
| Cytotoxicity | 0 Level |
| Radioactivity(Bq.g-1) | ＜0.1 |
| Sintering temperature(℃) | 1480-1510 Recommend 1500 |
Indications For Use ≤3 units
Sintering:
Factory Display:
Application:
Exhibition:
Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250