Organic Platinum Silicone Curing Agent Transparent Paste Two Component FDA Approved

Brand Name:KangLiBang
Certification:ROHS,SGS
Model Number:C-100AB
Minimum Order Quantity:5KG
Delivery Time:5-7days
Payment Terms:T/T
Contact Now

Add to Cart

Verified Supplier
Location: Shenzhen Guangdong China
Address: H Building, 3rd Xinwei Industrial Park, Dalang Street, Longhua New District, Shenzhen City, Guangdong Province, China.
Supplier`s last login times: within 1 hours
Product Details Company Profile
Product Details

Two Component Platinum Addition Type Cross Linking Agent


C-100AB,two component platinum addition type cross linking agent which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,The vulcanized products can pass the FDA test, ,it features with non-toxic, odourle


PRODUCT SPECIFICATION:

C-100A: transparent paste, containing platinum and organic silicon polymer

C-100B: transparent organic silicon polymer, containing crosslinking agent and inhibitor

Hardness(ShoreA) : 50±5

Tensile Strength (Mpa) : 10~12

Elongation at Break(%): 500~540 Compression Set %(100℃/22h): <5

Specific Gravity: 1.1g/cm3


PRODUCT DETAILS:


C-100AB,two component platinum addition type cross linking agent

Which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,

The vulcanized products can pass the FDA test,

it features with non-toxic, odourless, high grade of transparency, well anti-yellowing and other properties.

PRODUCT ADVANTAGE:

Food Grade and Medical Grade,No secondary curing

Anti-yellow,High penetration

Low addition rate



ATTENTION:


The raw material is easy poisoning once contact with nitrogen, phosphorus, sulfur and heavy metal materials.

C-100A and C-100B can not be added at the same time. First add C-100B into raw silicone and mixing evenly, then add C-100A into raw silicone. The addition order is important.

The temperature of mixing machine which used for mixing silicone with platinum curing agent can not be higher than 45. Please add this agent after being cold.

The mixed raw materials should be used up within two days

.Please choose the suitable raw materials for hot air vulcanization,unmatched raw material will cause bubbles in the process.


PROCESSING:


Type one: Extrusion Or Injection Moulding


  1. For High Tear Strength Silicone Materials (filled with gaseous phase white carbon black) Application weight ratio:

C-100B 2.0~2.5%

C-100A 0.5~0.6%


Curing condition: IR(6meters),constant temperature ±5. First curing: IR curing at 190~200 for 40~60 seconds.

Finished curing: After first curing, it should be cured again as below conditions.


Curing temperature

155~165

165~175Over 175
Curing time3~5minutes3minutes2minutes

  1. For Normal Silicone Material

Application weight ratio:

C-100B 1.5~2.0%

C-100A 0.5~0.6%

Curing condition:IR(6meters),constant temperature ±5.

First curing: IR(Infrared Radiation) curing at 140 for 40~50 seconds. Finished curing:After first curing, it should be cured again as below conditions.


Curing temperature


80~90


95~110


115~135


Curing time


7 minutes


5 minutes


4 minutes


Type two: Compression Molding


Application weight ratio:

C-100B 1.0~1.5%

C-100A 0.5%

Curing temperature: 115~135℃(200~300seconds)

Curing time:Can be adjusted with the thickness and type of the silicone products

China Organic Platinum Silicone Curing Agent Transparent Paste Two Component FDA Approved supplier

Organic Platinum Silicone Curing Agent Transparent Paste Two Component FDA Approved