Super Mirror Gold Stainless Steel Sheet Plate 201 304 1219Mm HL 2D
Brand Name:Vespolari Jiangsu
Certification:ISO SGS ROHS
Minimum Order Quantity:1Ton
Delivery Time:7-15 Days
Payment Terms:TT L/C
Place of Origin:Made in China
Contact Now
Add to Cart
Active Member
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
Super Mirror Gold Stainless Steel Sheet Plate 201 304
Type 304 Stainless Steel is the most widely used of the austenitic (chromium/nickel) stainless steels. In the annealed condition it is essentially non-magnetic and becomes slightly magnetic with the application of cold work. Type 304L Stainless Steel is preferred in welding applications to exclude the formation of chromium carbides during cooling in the heat affected region of the weld. These alloys represent an excellent combination of corrosion resistance and fabricability.
Online consultationProject Introduction
Type 304 Stainless Steelis the most widely used of the austenitic (chromium/nickel) stainless steels. In the annealed condition it is essentially non-magnetic and becomes slightly magnetic with the application of cold work. Type 304L Stainless Steelis preferred in welding applications to exclude the formation of chromium carbides during cooling in the heat affected region of the weld. These alloys represent an excellent combination of corrosion resistance and fabricability.
Specifications
Type 304 ASTM A240, ASTM A666, AMS 5513 Type 304L ASTM A240, ASTM A666, AMS 5511
Typical Applications
Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres
Chemical Composition: (Per ASTM A240)
| Product name | Super mirror gold Stainless Steel sheet plate 201 304 |
| Material | 201/201/304/304L/316/316L/321/309S/310S |
| Standard | JIS, AISI, ASTM, GB, DIN, EN |
| Length | 2000mm,2438mm,3048mm,6000mm or customized |
| Thickness | 0.1mm--3mm |
| Width | 600mm,1219mm,1250mm,1500mm,1800mm or customized |
| Surface finish | 2B,BA,HL,BK,NO.1,NO.4,8K,Embossed,Sandblast,Hairline,Etchedetc |
| Country of origin | China, shandong |
| Delivery time | 10-15 days after your deposit, or according the quantity |
Mechanical Properties: (Per ASTM A240, A666)
Type | Yield Strength 0.2% offset (KSI) | Tensile Strength (KSI) | % Elongation(2" Gauge length) | Hardness Rockwell |
304 Ann | 30 min. | 75 min. | 40 min. | HRB 92 max. |
304 Hard | 75 min. | 125 min. | 12 min. | HRC 25-32 (typical) |
304 Hard | 110 min. | 150 min. | 7 min. | HRC 32-37(typical) |
304L Ann | 25 min. | 70 min. | 40 min. | HRB 92 max. |
304L Hard | 75 min. | 125 min. | 12 min. | HRC 25-32 (typical) |
304L Hard | 110 min. | 150 min. | 6 min. | HRC 32-37 (typical) |
Physical Properties: (annealed)
304 & 304L | ||
Density (lb./ in^2) @ RT | 0.29 | |
Modulus of Elasticity in Tension (psi x 10^6) | 28.0 | |
Specific Heat (BTU/°F/lb.) | 32 to 212 °F | 0.12 |
Thermal Conductivity (BTU/hr/ft^2/ft) | 212°F | 9.4 |
932°F | 12.4 | |
Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F) | 32 to 212°F | 9.2 |
32 to 600°F | 9.9 | |
32 to 1,000°F | 10.2 | |
32 to 1,200°F | 10.4 | |
Electrical Resistivity (micro ohms - cm) | at 70°F | 72 |
Melting Point Range (°F) | 2550 to 2650 | |
Oxidation Resistance - Continuous Service(°F) | 1,650 | |
Oxidation Resistance - Intermittent Service(°F) | 1,500 |
Processing
Types 304 and 304L cannot be hardened by thermal tr