TINOX TPW-716 Hybrid Pigment 74% TiO₂ for High-Performance Coatings
Brand Name:TINOX
Certification:REACH ISO9001
Model Number:TPW-716
Minimum Order Quantity:20MT
Delivery Time:7DAYS
Payment Terms:L/C,D/P,T/T,Western Union,D/A
Contact Now
Add to Cart
Verified Supplier
Location:
Chengdu Sichuan
Address:
1st Floor, No.40, No.69, Zhengbei Middle Street, Huayang Street, Tianfu New District, Chengdu City, Sichuan,China
Supplier`s last login times:
within 39 hours
Product Details
Company Profile
Product Details
TINOX TPW-716 Hybrid Pigment White
Premium Performance Hybrid Pigment for Superior Coatings
TINOX TPW-716 is an advanced hybrid pigment based on rutile-type TiO₂, engineered specifically for high-performance paint and coating applications. Through a proprietary manufacturing process that combines premium TiO₂ pigment components with ultra-fine functional fillers, TPW-716 enhances light scattering efficiency while reducing TiO₂ consumption without compromising optical performance.
Exceptional Performance Advantages
Superior Optical PropertiesBrightness L* ≥ 96.0 with bluish undertone for exceptional whiteness and visual appeal | Excellent Gloss DevelopmentEnhanced surface reflectivity and gloss stability for premium finishes |
Strong Hiding PowerOutstanding coverage with reduced pigment loading requirements | Enhanced DurabilityImproved abrasion resistance, weather resistance, and coating film hardness |
Excellent DispersionHegman ≥ 6.5 for easy incorporation and reduced processing time | Environmental BenefitsLower CO₂ emissions per unit compared to pure TiO₂ |
Technical Specifications
| Parameter | Value |
|---|---|
| TiO₂ content | ≥74.0% |
| Rutile content | ≥99.0% |
| Brightness L* | ≥96.0 |
| Oil absorption | ≤20 g/100g |
| Relative Humidity (105°C) | ≤0.5% |
| Post-treatment | Al, Zr, P, organic |
| pH value | 6.5-8.5 |
Performance Validation
Based on comprehensive testing in the TINOX TPW Series brochure, TPW-716 demonstrates:
- Whiteness index nearly matching premium TiO₂ pigment R-2160
- Superior performance compared to standard TiO₂ pigment R-2140
- Excellent opacity levels comparable to pure TiO₂ pigments
- Outstanding gloss development for high-quality finishes
Recommended Formulation
High-Gloss Water-Based Acrylic Enamel (Based on Test Data)
| Component | Function | Content (%) |
|---|---|---|
| Deionized Water | Solvent | 18.0 |
| Dispersing Agent | Pigment dispersion | 0.6 |
| Wetting Agent | Surface tension reduction | 0.3 |
| TINOX TPW-716 | Primary pigment | 22.0 |
| Acrylic Emulsion (50%) | Binder | 45.0 |
| Coalescing Agent | Film formation | 2.5 |
| Defoamer | Foam control | 0.4 |
| Rheology Modifier | Viscosity control | 0.8 |
| Preservative | Biostability | 0.2 |
| Ammonia (28%) | pH adjustment | 0.2 |
| Water (adjustment) | Final adjustment | 10.0 |
Processing Instructions:
- Add water, dispersing agent, and wetting agent to mixing vessel
- Slowly add TINOX TPW-716 under moderate agitation (800-1000 rpm)
- Increase agitation speed to 1500-2000 rpm for 15-20 minutes until Hegman fineness ≥6.5 is achieved
- Reduce speed and slowly add acrylic emulsion
- Add coalescing agent, defoamer, rheology modifier, and preservative
- Adjust pH to 7.5-8.5 with ammonia solution
- Add remaining water to achieve desired viscosity
- Filter and package
Expected Performance (Based on Tinox Test Data):
- Whiteness Index: ≥96.5
- Gloss (60°): ≥85 GU
- Contrast Ratio: ≥0.98
- Yellowness Index: <1.5
- PVC: ~25%
Note: This formulation is based on test data from the TINOX TPW Series brochure, specifically the acrylic enamel paint tests with 75% emulsion content (PVC = 25%).
Contact Information
TINOX CHEMIE GMBH
Lütticher Straße 132, 40547 Düsseldorf, Germany
Tel: +49 (0)211 52809600
Email: jojo@tinoxchem.com
Web: www.tinoxchem.com
TINOX TPW-716 Hybrid Pigment 74% TiO₂ for High-Performance Coatings
Inquiry Cart
0