IATF16949 High Density Graphite Ingot Mould For Melting Casting Refining
Brand Name:NA
Certification:ISO9001; ISO14000; IATF16949
Model Number:NA
Minimum Order Quantity:10 pcs
Delivery Time:25-30 days
Payment Terms:L/C, D/A, D/P, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Zigong Sichuan China
Address:
99 Jinli Road, Bancang Industrial Park,Zigong 643000,Sichuan Province, China
Supplier`s last login times:
within 23 hours
Product Details
Company Profile
Product Details
Characteristic
1. As refractories: Graphite and its products have the properties of high temperature resistance and high strength. Graphite crucibles are mainly used in metallurgical industry. Graphite is often used as protective agent for ingots and lining of metallurgical furnaces in steel making.
2. Conductive material: used in the electrical industry as the coating of electrodes, brushes, carbon rods, carbon tubes, mercury positive current, graphite gaskets, telephone parts, television picture tubes, etc.
3. As wear-resistant and lubricating material: Graphite is often used as lubricant in mechanical industry
Recommended range of mechanical carbon and applicable working conditions
| Model | Equipment | Application | Friction material | Working medium | Technical conditions (not greater than) |
| M106H | Centrifugal pump Compressor Flow meter | Face seal Piston ring Bearing | Tungsten carbide Cast iron bronze Hard alloy Chrome-plated steel Silicon carbide Silicon nitride | Alkaline medium such as oil,water,high temperture,high pressure steam,salt slurry water containing crystal particles,ammonia sulfide,propane,liquid ammonia,30% potassium carbonate solution,50% sodium hydroxide solution | Rotating speed:12000R.P.M Temperature:200℃ Medium pressure:3MPa PV Value:12MPa/m/s |
| M106K | |||||
| M158K | |||||
| M120H | Centrifugal pump Compressor Boiler preheater Submersible pumps Vacuum pumps | Face seal Piston ring Bearing Explosion-proof membrane Rotary van | Tungsten carbide Cast iron bronze Hard alloy Chrome-plated steel Silicon carbide Silicon nitride | Oil,water,air,weak acid,weakly alkaline medium,M120k use a normal concentration of sulfuric acid medium | Rotating speed:29000R.P.M Temperature:200℃ Medium pressure:3MPa PV Value:8MPa/m/s |
| M120K | |||||
| M254H | Centrifugal pump Flow meter Cigarette machine Compressor Fermenter turbine | Face seal Piston ring Bearing Gas distribution plate | Ceramic Hard alloy Bronze Stainless steel Chrome-plated steel | Oil,water,organic acids,alkalis,salt etc. | Rotating speed:29000R.P.M Temperature:200℃ Medium pressure:2MPa |
| M254K | |||||
| M106P | Steam flow meter High temperature hot oil pump Aircraft engine Mailbox Starter motor Cigarette machine Fan | Face seal Bearing Gas dirtribution plate Electric locomotive skateboard | Ceramic Hard alloy Bronze Stainless steel Chrome-plated steel Alloy steel | Dry friction,water,high temperature water,sea water,water vapor,organica oil | Temperature:-200-+400℃ |
| M120P | |||||
| M106D | Clean water pump Nuclear secondary pump Boiler feed pump drying furnace Power equipment | Face seal Bearing Bushing | Cast iron Hard alloy Stainless steel Chrome-plated steel Silicon carbide Silicon nitride | Air,oil,water,acid,alkali salt.etc. | Rotating speed:5000R.P.M Temperature:500℃ Medium pressure:5MPa |
| M120D | |||||
| M254D |
| Category | Model | Impregnant | Shore Hardess | Flexural Strength | Compressive Strength | Porosity | Bulk Density | Thermal expansion coeffcient | Temp. | |||
| ≥ | `X | ≥MPa | `X | ≥MPa | `X | ≤% | g/cm3 | 10-6/℃ | ℃ | |||
| Graphite | M120 | - | 60 | - | 25 | - | 81 | - | 18 | 1.6 | 4 | 350 |
| M154 | - | 40 | - | 20 | - | 40 | - | 28 | 1.42 | - | 350 | |
| M254 | - | 10 | - | 25 | - | 45 | - | 25 | 1.65 | 3.4 | 450 | |
| Impregnated resin carbon graphite | M106H | Epoxy resin | 75 | 90 | 51 | 60 | 180 | 190 | 1.0 | 1.62 | 4.8 | 200 |
| M238H | 40 | 55 | 39 | 50 | 78 | 110 | 1.0 | 1.85 | 4.5 | 250 | ||
| M255H | 40 | 50 | 34 | 45 | 78 | 90 | 1.0 | 1.8 | 4.5 | 200 | ||
| M106K | Furan resin | 80 | 95 | 55 | 65 | 200 | 210 | 2.0 | 1.62 | - | 200 | |
| M120K | 75 | 95 | 50 | 60 | 190 | 195 | 2.0 | 1.7 | 200 | |||
| M154K | 60 | 35 | 70 | 6.0 | 1.6 | 200 | ||||||
| M158K | 80 | 90 | 54 | 60 | 200 | 210 | 1.2 | 1.65 | - | 200 | ||
| Impregnated metal carbon graphite | M106D | Antimony alloy | 75 | - | 55 | 65 | 170 | 190 | 3 | 2.2 | 5.0 | 500 |
| M120D | 70 | - | 50 | 60 | 140 | 160 | 3 | 2.2 | 5.0 | 500 | ||
| M254D | 35 | - | 35 | - | 65 | - | 3 | 2.2 | 4.5 | 500 | ||
| M120P | Copper alloy | 65 | - | 65 | - | 200 | - | 3 | 2.4 | - | 400 | |
| Impregnated glass carbon graphite | M106R | Glass | 110 | - | 75 | - | 210 | - | 1.5 | 1.9 | 4.67 | 600 |
| M120R | 95 | - | 57 | - | 190 | - | 1.5 | 1.9 | 4.67 | 600 | ||
| M254R | 65 | - | 55 | - | 100 | - | 1.5 | 1.9 | - | 600 | ||
| M262R | 75 | - | 48 | - | 138 | - | 1.5 | 1.9 | - | 600 | ||
| Hot pressed graphite | M353 | - | 45 | - | 45 | - | 120 | - | 1.0 | 1.75 | - | 100 |
| M352 | - | 35 | - | 35 | - | 80 | - | 1.0 | 1.75 | - | 100 | |
| M356 | - | 50 | - | 50 | - | 140 | - | 1.0 | 1.75 | - | 100 | |
| M357 | - | 40 | - | 40 | - | 80 | - | 1.0 | 1.75 | 9.0 | 100 | |