17-7PH Stainless Steel Plate Hot Rolled 3.0 - 40.0mm SS Custom Laser Cutting

17-7PH Stainless Steel Plate Hot Rolled 3.0 - 40.0mm SS Plate Custom Laser Cutting

17-7 PH is a precipitation-hardened stainless steel that is well suited for aerospace and other applications requiring high strength and good corrosion resistance and formability. Type 17-7 PH is a Chromium-Nickel-Aluminum, austenitic stainless steel. It is the most formable of all PH grades and has the highest strength and hardness. It is less magnetic than other PH grades and offers minimal distortion upon heat treatment. This material maintains its valuable properties at temperatures up to 800° F (427° C).

Stainless Steel 17-7PH is available in three conditions – RH 950 and TH 1050, which can be hardened to high strength levels with simple heat treatments, and CH 900 which should be used in high-strength parts where excellent ductility and workability is not required.

We offers Stainless Steel 17-7PH in four sub-type specifications and multiple shapes/forms:

• AMS 5528 (Plate, Sheet, and Strip)
• AMS 5529 (Sheet and Strip)
• AMS 5568 (Tubing)
• AMS 5644 (Bar and Forging)

Chemical Composition of Stainless Steel 17-7PH

*Not exclusively to the element mentioned, but that one predominates other elements that are used only in minimal quantities.

Fabrication and Working Instructions

Stainless Steel 17-7PH hardens rapidly during heat treatment and requires intermediate annealing in deep drawing or in forming intricate parts. In some conditions, like Condition C, for example, this steel can be very hard and strong, which means that advanced fabrication techniques for such materials should be used.

As for machining, special care must be applied to the speed at which the parts are machined. 17-7PH Stainless Steel can display long gummy chips during machining, and therefore slower speeds are recommended, accompanied by constant feeds.

17-7PH Stainless Steel can be welded by all conventional fusion and resistance techniques. However, if optimum mechanical properties are wanted, special care is recommended to find the best heat-treated conditions that should be done during the welding. The following heat treatments of the welded part are also essential for excellent mechanical properties. More precisely, austenite conditioning and precipitation hardening are mandatory after the welding is finished to obtain high strength.

Overall, 17-7PH is not as weldable as 17-4PH Stainless Steel. The reason for this is the high concentration of Aluminum, which deteriorates penetration of the weld, thus creating a bond that is not as strong. Weld slug formation can also be worsened during arc welding, which is another area that requires special care.

Mechanical Properties of 17-7PH stainless steel

Thermal Properties

Heat Treatment

Stainless Steel 17-7PH can be heat treated and annealed in electric furnaces, radiant tube furnaces that work both on oil and gas, and vacuum furnaces. The use of furnaces that use oil or natural gas fire is not recommended. Given the fact that 17-7PH doesn’t work well in reducing environments, heat treatment, and annealing in such atmospheres should be avoided. These atmospheres may be responsible for nitriding of the surface. If bright annealing is required, dry hydrogen, argon or helium atmosphere can be used at cooling rate of -65° F (-54° C).

Depending on the condition, different heat treatments of 17-7PH are recommended:

• Condition A – mill Annealed at 1950 ± 25° F (1066 ± 14° C).
• Condition A1750 – mill Annealed at 1950 ± 25° F (1066 ± 14° C), then heat to 1750 ± 15° F (954 ± 8° C) for 10 minutes and air cool to room temperature.
• Condition T – mill Annealed at 1950 ± 25° F (1066 ± 14° C), then heat to 1400 ± 25° F (760 ± 14° C) and hold for 90 minutes. Finally, cool to 60° F (16° C) within 1 hour and hold for 30 minutes.
• Condition TH 1050 – mill Annealed at 1950 ± 25° F (1066 ± 14° C), then heat to 1400 ± 25° F (760 ± 14° C) and hold for 90 minutes. Next, cool to 60° F (16° C) within 1 hour and hold for 30 minutes. Finally, heat to 1050 ± 10° F (566 ± 5.5° C) and hold for 90 minutes, then air cool to room temperature.
• Condition R 100 – mill Annealed at 1950 ± 25° F (1066 ± 14° C), then heat to 1750 ± 15° F (954 ± 8° C) for 10 minutes and air cool to room temperature. Within 1 hour, start cooling to -100 ± 10° F (73 ± 5.5° C) and hold for 8 hours before air warming to room temperature.
• Condition RH 950 – the same as Condition R 100 only with added precipitation hardening at 950 ± 10° F (510 ± 5.5° C) for 60 minutes and then air cooling to room temperature.

Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe best-selling consumer market. Without our products among consumers enjoy a higher status, the company with a number of retailers and agents to establish a long-term stable cooperative relationship. Our distribution of stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe variety complete, reasonable price. The strength of the company, heavy credit, abide by the contract, ensure product quality, with a variety of management characteristics and the principle of small profits, to win the trust of our customers.