Customizable Car Battery Thermal Wrap 70 Shore A Hardness Soft Silicone Rubber Sheet
Brand Name:FQ
Certification:IATF16949
Model Number:Rubber 1
Minimum Order Quantity:3000
Delivery Time:1000 pcs/ days
Payment Terms:L/C, T/T, D/P
Contact Now
Add to Cart
Verified Supplier
Address:
No. 188, Wuchen Road, Dongtai Industrial Park, Qingkou Town, Minhou County
Supplier`s last login times:
within 2 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
Battery Wrapping Flame Hardness Shore A Barrier Films High Flame Retardant Silicone Rubber Battery Thermal Wrap
Silicone foam insulation has emerged as a superior solution for battery protection and thermal management systems in the rapidly evolving field of new energy vehicles (NEVs). This article delves into the inherent advantages of silicone foam insulation, highlighting its unique capabilities and why it surpasses traditional materials. By understanding its benefits, we can explore its critical role in enhancing NEV battery performance, safety, and longevity.
Excellent Resilience:
Silicone foam insulation boasts exceptional resilience, making it
an ideal choice for battery protection. Experimental data reveals
that even after undergoing 8,000 cycles of compression, the
material experiences minimal deformation, with less than 5% change.
This outstanding rebound property ensures long-term effectiveness
and reliability, safeguarding NEV batteries throughout their
operational lifespan.
Comprehensive Prtection:
Silicone foam insulation provides more than just insulation. It
offers additional advantages, including dustproofing,
waterproofing, heat dissipation, and shock absorption. These
properties are pivotal for NEV battery protection systems,
shielding the battery pack from external contaminants, preventing
moisture ingress, efficiently managing heat generated during
operation, and minimizing the impact of vibrations and shocks. Such
comprehensive protection contributes to the overall performance,
safety, and durability of NEV batteries.
Unyielding Performance under Extreme Conditions:
Silicone foam insulation undergoes rigorous testing to evaluate its
performance under harsh environmental conditions. Experimental data
from stress relaxation tests conducted at 85°C and 85% relative
humidity for 1,000 hours demonstrates that the material exhibits a
stress relaxation rate of only 20.98%. This exceptional result
attests to its ability to maintain mechanical integrity and provide
consistent performance, even in demanding situations. NEV batteries
can rely on silicone foam insulation to deliver unwavering
protection, regardless of challenging operating conditions.
Superior Compression Resistance:
Silicone foam insulation has excellent resistance to crushing and
retains its shape and performance even after extensive use. The
material exhibits a consistently low compression set, ranging from
0.34% to 0.72% in a 10,000-belt 1 million compression cycle test,
ensuring its long-lasting durability and effectiveness in
protecting new energy vehicle batteries.
These results highlight the material's resilience and ability to maintain its shape and performance, even after prolonged use. NEV batteries benefit from the long-lasting durability provided by silicone foam insulation.
Minimal Water Absorption:
Silicone foam insulation exhibits an impressively low water
absorption rate of only 0.266%. This characteristic is crucial in
NEV battery protection, as it ensures the material remains stable
and unaffected by moisture. The low water absorption rate prevents
any adverse effects on the battery pack's performance, even in
humid environments. It further reinforces the material's
suitability for NEV applications.
As the NEV industry continues to advance, silicone foam insulation emerges as the optimal choice for battery protection and thermal management systems. Its exceptional resilience, comprehensive protection features, unyielding performance under extreme conditions, superior compression resistance, and minimal water absorption set it apart from traditional materials. Silicone foam insulation plays a pivotal role in enhancing NEV battery performance, safety, and longevity. Its numerous advantages make it a compelling solution that should be widely adopted in the NEV industry, driving innovation and ensuring the continued success of new energy vehicles.
Main Features
70 Shore A Hardness Blue Color Silicone Rubber Sheet
- 70 Shore A hardness blue color silicone rubber sheet is ideal for high and low-temperature applications. The electrical properties of 70 Shore A hardness blue color silicone rubber sheet are excellent and resistance to weathering and ozone attack is outstanding. It is not resistant to super-heated steam. Its physical properties are generally low but are at least retained at higher temperatures. Gas permeability is very poor as is resistance to petroleum based fluids. 70 Shore A hardness blue color silicone rubber sheets are expensive in comparison to most other rubbers. Food Quality/FDA compliant grades are available for use in the food and pharmaceutical industries.
Specification
The main performance parameters are shown in Table
| Serial number | Test items | Unit | Test Standard | SR No. | |||
| SR 35-A | SR 40-A | SR 50-A | SR 60-A | ||||
| 1 | Hardness | Shore A | GB/T531.1-2008 | 35±7 | 40±10 | 50±10 | 60±10 |
| 2 | Density | g/cm3 | 4.3.2 | 0.8≤μ±3σ≤1.4 | 1.00≤μ±3σ≤1.51 | 1.00≤μ±3σ≤1.51 | 1.1≤μ±3σ≤1.5 |
| 3 | 25℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.25≤μ±3σ≤0.75 | 10%: 0.45≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.63≤μ±3σ≤1.77 | 20%: 0.95≤μ±3σ≤1.45 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.20≤μ±3σ≤2.24 | 30%: 1.50≤μ±3σ≤2.50 | ||||
| 4 | 25℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 5 | 25℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 6 | -30℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.08≤μ±3σ≤.0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.65 | 10%:0.55≤μ±3σ≤0.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.90≤μ±3σ≤1.20 | 20%:1.10≤μ±3σ≤1.95 | ||||
| 30%:0.45≤μ±3σ≤0.9 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.50≤μ±3σ≤2.00 | 30%: 2.00≤μ±3σ≤3.95 | ||||
| 7 | -30℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 8 | -30℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 9 | 60℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.70 | 10%: 0.35≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.80≤μ±3σ≤1.30 | 20%:0.65≤μ±3σ≤1.60 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.00≤μ±3σ≤2.10 | 30%: 1.00≤μ±3σ≤2.50 | ||||
| 10 | 60℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 11 | 60℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 12 | Double 85 post-aging compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.50≤μ±3σ≤0.70 | 10%: 0.40≤μ±3σ≤1.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.90≤μ±3σ≤1.30 | 20%: 1.00≤μ±3σ≤3.20 | ||||
| 30%:0.45≤μ±3σ≤0.75 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.40≤μ±3σ≤2.10 | 30%: 1.70≤μ±3σ≤5.50 | ||||
| 13 | Double 85 post-aging shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 14 | Double 85 post-ageing Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 15 | Compression curve after high and low-temperature cycle | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.45≤μ±3σ≤0.65 | 10%: 0.50≤μ±3σ≤2.20 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.85≤μ±3σ≤1.35 | 20%: 1.00≤μ±3σ≤4.00 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.30≤μ±3σ≤2.50 | 30%: 1.80≤μ±3σ≤6.80 | ||||
| 16 | Shear performance under pressure after high and low temperature | MPa | ASTM C273C /273M-16 | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 |
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 17 | Tensile strength after high and low-temperature cycle | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 18 | Flame retardant | / | UL94 | UL94 V0(2mm) | V0(t≥2mm) | V0(t≥2mm) | V0(t≥2mm) |
| V1(1≤t＜2mm) | V1(1≤t＜2mm) | V1(1≤t＜2mm) | |||||
| HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | |||||
| 19 | Forbidden object | / | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV |
| 20 | Insulation | MΩ | 1000V DC 60s | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 |
| 21 | Impedance | mA | 2700V DC 60s | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 |
| 22 | Thermal conductivity | W/(m·K) | GB/T 10295-2008 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 |
| 23 | Specific heat capacity | J/(g·K) | ASTM E1269-2011 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 |
| 24 | Stress retention rate | % | GB/T1685-2008 | ≥40 | ≥40 | ≥40 | ≥40 |
| 25 | 25℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.8 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 26 | -30℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 27 | 60℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥0.6 | Min≥1.5 |
| 28 | Double 85 ageing shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 29 | Shear strength after high and low-temperature cycles with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
Industries
• Agriculture and Livestock• Mining and Quarrying
• Mineral Processing
• Power Generation
• Construction
• Oil and Gas
Package & Delivery
Customizable Car Battery Thermal Wrap 70 Shore A Hardness Soft Silicone Rubber Sheet
Inquiry Cart
0