OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet
Brand Name:FQ
Certification:IATF16949
Model Number:Rubber 1
Minimum Order Quantity:Customized
Delivery Time:1000 pcs/ days
Payment Terms:L/C, T/T, D/P
Contact Now
Add to Cart
Active Member
Address:
No. 188, Wuchen Road, Dongtai Industrial Park, Qingkou Town, Minhou County
Supplier`s last login times:
within 2 hours
Product Details
Company Profile
Product Details
Battery Wrapping Flame Barrier Films High flame retardant silicone rubber battery thermal wrap
Main Features
It is used to realize buffering energy absorption between battery pack cells.
- Jelly Roll Insulation
- Top Cap Insulation
- Separator Papers
- Tab & Lead insulation
- Pouches
- Thermal Insulation
- Thermal Runaway Protection
- Go-Therm Thermal Runaway Barrier
Specification
The main performance parameters are shown in Table
| Serial number | Test items | Unit | Test Standard | SR No. | |||
| SR 35-A | SR 40-A | SR 50-A | SR 60-A | ||||
| 1 | Hardness | Shore A | GB/T531.1-2008 | 35±7 | 40±10 | 50±10 | 60±10 |
| 2 | Density | g/cm3 | 4.3.2 | 0.8≤μ±3σ≤1.4 | 1.00≤μ±3σ≤1.51 | 1.00≤μ±3σ≤1.51 | 1.1≤μ±3σ≤1.5 |
| 3 | 25℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.25≤μ±3σ≤0.75 | 10%: 0.45≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.63≤μ±3σ≤1.77 | 20%: 0.95≤μ±3σ≤1.45 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.20≤μ±3σ≤2.24 | 30%: 1.50≤μ±3σ≤2.50 | ||||
| 4 | 25℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 5 | 25℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 6 | -30℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.08≤μ±3σ≤.0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.65 | 10%:0.55≤μ±3σ≤0.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.90≤μ±3σ≤1.20 | 20%:1.10≤μ±3σ≤1.95 | ||||
| 30%:0.45≤μ±3σ≤0.9 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.50≤μ±3σ≤2.00 | 30%: 2.00≤μ±3σ≤3.95 | ||||
| 7 | -30℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 8 | -30℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 9 | 60℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.70 | 10%: 0.35≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.80≤μ±3σ≤1.30 | 20%:0.65≤μ±3σ≤1.60 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.00≤μ±3σ≤2.10 | 30%: 1.00≤μ±3σ≤2.50 | ||||
| 10 | 60℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 11 | 60℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 12 | Double 85 post-aging compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.50≤μ±3σ≤0.70 | 10%: 0.40≤μ±3σ≤1.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.90≤μ±3σ≤1.30 | 20%: 1.00≤μ±3σ≤3.20 | ||||
| 30%:0.45≤μ±3σ≤0.75 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.40≤μ±3σ≤2.10 | 30%: 1.70≤μ±3σ≤5.50 | ||||
| 13 | Double 85 post-aging shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 14 | Double 85 post-ageing Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 15 | Compression curve after high and low-temperature cycle | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.45≤μ±3σ≤0.65 | 10%: 0.50≤μ±3σ≤2.20 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.85≤μ±3σ≤1.35 | 20%: 1.00≤μ±3σ≤4.00 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.30≤μ±3σ≤2.50 | 30%: 1.80≤μ±3σ≤6.80 | ||||
| 16 | Shear performance under pressure after high and low temperature | MPa | ASTM C273C /273M-16 | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 |
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 17 | Tensile strength after high and low-temperature cycle | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 18 | Flame retardant | / | UL94 | UL94 V0(2mm) | V0(t≥2mm) | V0(t≥2mm) | V0(t≥2mm) |
| V1(1≤t＜2mm) | V1(1≤t＜2mm) | V1(1≤t＜2mm) | |||||
| HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | |||||
| 19 | Forbidden object | / | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV |
| 20 | Insulation | MΩ | 1000V DC 60s | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 |
| 21 | Impedance | mA | 2700V DC 60s | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 |
| 22 | Thermal conductivity | W/(m·K) | GB/T 10295-2008 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 |
| 23 | Specific heat capacity | J/(g·K) | ASTM E1269-2011 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 |
| 24 | Stress retention rate | % | GB/T1685-2008 | ≥40 | ≥40 | ≥40 | ≥40 |
| 25 | 25℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.8 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 26 | -30℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 27 | 60℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥0.6 | Min≥1.5 |
| 28 | Double 85 ageing shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 29 | Shear strength after high and low-temperature cycles with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
- Available in – Continuous rolls or cut sheets
- Durometers available – 70
- Thicknesses available (in) – 0.0625 to 0.25
- Typical roll lengths (ft) – 50 to 100
- Typical roll widths (in) – 36 & 48
- Surface finishing – Smooth finish, both sides
- Color – Black
Typical Applications
- Ev Battery Pack Structure is Fireproof and Insulated;
- Aerospace Cargo Fire Covers;
- A Protective Layer of the Brake Line of Railway Vehicles;
- Fire Barrier Between Railway Passenger Cars.