Engineering Machinery Epoxy Primer Water Borne Paint
Brand Name:HAOLISEN
Delivery Time:30-60 Days
Payment Terms:T/T
Packaging Details:50kg、60 kg、200kg、1000kg packaging barrels
Place of Origin:Shanghai China （Mainland）
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
15/F, No.1185, Huyi Road, Jiading District, Shanghai，China.
Supplier`s last login times:
within 1 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
Water borne paint for Engineering Machinery
Cooperation Client Directory:Zoomlion；SANY；XCMG
Advantages: High performance; Low VOCs
Product Specification
- Type: High adhesion epoxy primer
- Product introduction
High adhesion epoxy primer hh3012a, is a new generation of two-component high adhesion epoxy primer coating developed by Haorisen Coatings (Shanghai) Co., Ltd .; low solvent content, no lead, cadmium, chromium, mercury For heavy metals, the paint film has the characteristics of good adhesion, good flexibility, and excellent corrosion resistance; this series of products can be coated on the surface of more metal substrates.
Scope of application
The product is mainly used for metal materials and surface-treated metal substrate surfaces.
Technical index
3.1 Technical Specifications of Original Paint
| Serial number | project | Main paint | Hardener |
| 1 | Density (g / ml) | 1.5±0.2 | 0.92±0.1 |
| 2 | Supply viscosity (25 ° C, tu4 #) | ≤40S | ≤40S |
| 3 | Solid weight | 78±3% | 53±3% |
| 4 | Construction period | >4h | |
Fourth, the construction process parameters
1.Applicable substrate: metal material and surface treated metal substrate surface.
Matching ratio
| High adhesion epoxy primer hh3012a | Curing agent hh3012b | Thinner hh3002c | |
| Ratio (mass ratio) | 6 | 1 | 0%-5% |
3.Suitable construction environment temperature and humidity: temperature 10-35 ℃, humidity 30-70% rh.
4.Substrate treatment: No oil and dust particles on the substrate.
5.Applicable construction methods: mixed air spray, air spray, airless spray.
6.Flash drying time: 5-10min / room temperature.
7, curing conditions: self-drying at room temperature / 65 ℃ * 20min.
8.Personnel protection: Construction personnel need to wear labor protection supplies.
- Precautions
1.Using cleaning agents can be used for appliance cleaning.
2.It is harmful to human health after inhalation. Please take safety measures during construction., storage, packaging and transportation
This product is a high solid coating, dangerous goods; prevent direct sunlight during transportation; packaging in 200l, 50l, 20l, 10l iron drums; keep the drums clean and hygienic during transportation and storage, and avoid carrying them into the drums during the feeding process. Dirt; if the packaging is damaged, you need to re-check the quality of the products in it.The products should be stored indoors, kept ventilated and dry to prevent freezing and overheating. The storage temperature should be controlled at 5 ~ 35 ℃. If the storage period is exceeded, the experiment should be used to determine whether it can continue to be used.
- Type: High solid polyurethane topcoat
一,Product introduction
High solid polyurethane gray topcoat hj3417a, is a new generation of two-component high solid polyurethane coatings developed by Hao Lisen Coatings (Shanghai) Co., Ltd. Good adhesion, good flexibility, good weather resistance, etc .; has excellent decoration and protection.
Scope of application
The product is mainly used for epoxy primer surface.
二,Technical index
3.1 Technical Specifications of Original Paint
| Serial number | project | Main paint | Hardener |
| 1 | Density (g / ml) | 1.12±0.2 | 1.05±0.1 |
| 2 | Supply viscosity (25 ° C, tu4 #) | ≤40S | ≤40S |
| 3 | Solid weight | 70±3% | 70±3% |
| 4 | Construction period | >4h | |
三, the construction process parameters
1.Applicable substrate: epoxy primer surface.
Matching ratio
| High solid polyurethane finish (gray) hj3417a | Curing agent hh3416b | Thinner hh3416c | |
| Ratio (mass ratio) | 3.5 | 1 | 0%-5% |
3.Suitable construction environment temperature and humidity: temperature 10-35 ℃, humidity 30-70% rh.
4.Substrate treatment: No oil and dust particles on the substrate.
5.Applicable construction methods: mixed air spray, air spray, airless spray.
6.Flash drying time: 10min
7, curing conditions: self-drying at room temperature / 70 ℃ * 30min.
8.Personnel protection: Construction personnel need to wear labor protection supplies.
五,Precautions
1.Using cleaning agents can be used for appliance cleaning.
2.It is harmful to human health after inhalation. Please take safety measures during construction.
六, storage, packaging and transportation
This product is a high solid coating, dangerous goods; prevent direct sunlight during transportation; packaging in 200l, 50l, 20l, 10l iron drums; keep the drums clean and hygienic during transport and storage, and avoid carrying the Dirt; if the packaging is damaged, you need to re-check the quality of the products in it.The products should be stored indoors, kept ventilated and dry to prevent freezing and overheating. The storage temperature should be controlled at 5 ~ 35 ℃. If the storage period is exceeded, the experiment should be used to determine whether it can continue to be used.
- Type: Polyaspartic acid ester topcoat
一,Product introduction
Poly aspartic acid ester topcoat, composed of a new type of polyaspartic acid ester resin and isocyanate curing agent and various anti-corrosive fillers and additives. High solid content, excellent adhesion to different primers It can be cured normally at low temperature of -10 ℃. No baking, energy saving, low construction VOCs, and meet the green coating standards.
二,Scope of application
The product is mainly used on primed metal materials.
三, performance technical indicators
3.1 Technical Specifications of Original Paint
| Serial number | project | index | Inspection standards | |
| 1 | Original paint state | Uniform without agglomeration, no mechanical impurities | Visual inspection after stirring | |
| 2 | Original paint viscosity | Stormer, 25 ° C, ku | 40-80 | GB/T1723 |
| 3 | Fineness | um | ≤20 | GB/T1724 |
| 4 | Solid content | % | ≥85 | GB/T1725 |
| 5 | proportion | Kg/L | 1.0-1.5 | GB/T6750 |
| 6 | Hiding power | g/㎡ | Black finish ≤ 45, other finishes ≤ 100 | GB/T1726 |
3.2 Composite Coating Performance Technical Index
| Serial number | project | Coating system technical indicators | Detection method | |
| 1 | Coating general performance | Color chromatic aberration | △ e≤1.0 Compared with standard swatches, no visible color difference is required. | Colorimeter |
| 2 | Coating thickness | 85 ~ 130 (μm) (composite coating) | GB/T13452.2 | |
| 3 | Gloss | Medium light: 60 ~ 75 (60 ° ∠) High light: 80-90 (60 ° ∠) | GB/T9754 | |
| 4 | Adhesion | Crossing method ≤ 1 level | GB/T9286 | |
| 5 | hardness | (Pencil method) ≥h | GB/T6739 | |
| 6 | Flexibility | ≤3mm (composite coating film thickness 100μm) | GB/T 1731 | |
| 7 | Impact resistance | ≥30kgcm (1kg, positive punching, composite coating film thickness 100μm) | GB/T1732 | |
| 8 | Coating resistance to media | Water resistance | Water immersion method (23 ± 2 ℃) 500hr, no rust, no foaming, adhesion ≤ 1 grade, pencil hardness greater than F | GB/T1733 |
| 9 | Alkali resistance | (25 ℃ 0.1N NaOH) 48hr, no foam, no wrinkle, slight discoloration and loss of light allowed | gb / t9274 (A method) | |
| 10 | Acid resistance | (25 ℃ 0.1NH 2 SO 4) 48hr, no bubbles, no wrinkles, slight discoloration and loss of light allowed | gb / t9274 (A method) | |
| 11 | Diesel resistance | 500hr, no rust, no blistering, adhesion ≤ 1 grade, pencil hardness greater than F | gb / t9274 (A method) | |
| 12 | Coating durability | Resistance to artificial accelerated aging | (Q-SUN) ≥2000hr filtered xenon arc radiation; no cracking, no chalking, no foaming, very slight discoloration allowed (△ Ecmc≤3.0), loss of light (≤20%) | gb / t1865 method 1 |
| 13 | Resistance to neutral salt spray | 1000hr; single side rust width ≤ 2mm at the scratch, no blistering, no rusting, no falling off | GB/T1771 | |
| 14 | Humidity and heat resistance | 960hr, no blistering, no rusting or cracking on the surface of the board, allowing slight discoloration (△ Ecmc≤3.0) | GB/T1740 | |
| 15 | Natural exposure | 3 years, loss of light rate ≤ 30% (allowing slight polishing according to item 7.4 of GB / T9276), very slight discoloration △ Ecmc ≤ 3.0, chalking level 1, cracking 1S1, foaming 1S1 | GB/T9276 | |
四,Construction process parameters
1.Applicable substrate: metal substrate after applying different primers.
Matching ratio
| Binder | Hardener | |
| Ratio (volume ratio) | 1-5 | 1 |
3.Suitable construction environment temperature and humidity: temperature 5-35 ℃, humidity 45-85% rh.
4.Substrate treatment: No oil and dust particles on the substrate.
5.Applicable construction methods: air spray, air-mix spray, airless spray, electrostatic spray.
6.Products with different drying speeds can be designed according to the customer's construction needs.
7.Personnel protection: Construction personnel need to wear labor protection supplies.
五,Precautions
1.Using cleaning agents can be used for appliance cleaning.
3.It is harmful to human health after inhalation. Please take safety measures during construction.
六, storage, packaging and transportation
Avoid direct sunlight during transportation and avoid freezing (> 5 ℃); packaging is 200l, 50l, 20l, 10l plastic drums or iron drums; keep the drums clean and hygienic during transportation and storage, and avoid carrying them into the drums during the feeding process If the packaging is damaged, you need to re-check the quality of the products.The products should be stored indoors, kept ventilated and dry to prevent freezing and overheating. The storage temperature should be controlled at 5 ~ 35 ℃. From the date of storage beyond the expiration date, it should be experimentally determined whether it can be continued to use.