Safety Electrophoretic Paint For Casting , Ed Coating Reduce The Amount Of Solvent
Brand Name:HAOLISEN
Certification:IATF16949 , ISO9001
Model Number:HLS-1701BLB/HLS-1701B
Minimum Order Quantity:Negotiation
Delivery Time:30-60 Days
Place of Origin:Shanghai China （Mainland）
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
15/F, No.1185, Huyi Road, Jiading District, Shanghai，China.
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
Solution for valve electrophoretic paint
Product Introduction :
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. |
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal |
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc. |
This product features shown below :
The appearance of the coating is flat, delicate, smooth, uniform high gloss.
Good stability of bath can adaptable for a longer updating cycle.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Ideal for high demand for salt spray industry, such as pipe trench, auto chassis parts, castings.
Main ingredients :
Matrix resin:acrylic modified epoxy resin |
Curing agent:totally enclosed multi-isocyanates |
Additives:surface active agent, prevent shrinkage cavity agent |
Pigment:Titanium pigment, Organic pigment, kaolin, antirust pigment |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.