Bicycle White Cationic Electrolysis Coating Strong Anti - Corrosion Property
Brand Name:HAOLISEN
Certification:IATF16949 , ISO9001
Model Number:HR-4000BLB
Minimum Order Quantity:Negotiation
Delivery Time:30-60 Days
Place of Origin:Shanghai China （Mainland）
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
15/F, No.1185, Huyi Road, Jiading District, Shanghai，China.
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
Special Bicycle white electrophoresis paint
Product Introduction :
HR-4000BLB Epoxy acrylic Color Cationic Electrocoat is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating, such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.
This product features shown below :
1, The bath has strong anti-shrinkage and anti-pollution ability
2, Good stability of bath can adaptable for a longer updating cycle
3, Coating fullness of good, better substrate hiding
4, Strong anti-corrosion propertie
Main ingredients :
1, Curing agent: totally enclosed multi-isocyanates
2, Solvent: alcohol ether
3, Pigment: Titanium pigment, Organic pigment, kaolin, antirust
pigment
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1400.00
Paste 233.00-175.00
DI water 1785.00
Total 3418.00-3360.00
⑵ Ripening conditions
Sample quantity: 3000～3500g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of parts coated)
Construction equipment
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Bicycle White Cationic Electrolysis Coating Strong Anti - Corrosion Property