GH5188 Cobalt Nickel Alloy for Application below 1100°C UNS R30188
GH 5188 is a cobalt-based alloy which possesses a unique
combination of properties. It has excellent high temperature
strength and oxidation resistance to 2100°F (1150°C) combined with
good post-aging ductility.
It has average room temperature tensile properties in the bright
annealed condition of 137.2 ksi (946 MPa) ultimate strength, 67.3
ksi (464 MPa) yield strength and 53% elongation. At 1800°F (980°C)
the alloy has ultimate and yield strengths of 35.2 ksi (243 MPa)
and 19.0 ksi (131 MPa), respectively, with 59% elongation.
Cryogenic temperatures do not significantly affect the ductility of
alloy 188, but strength levels are increased markedly.
The excellent oxidation resistance of GH5188 results from minute
additions of lanthanum, which modifies the protective oxide scale
in such a manner that the oxide becomes extremely tenacious and
retards diffusion when exposed to temperatures through 2100°F
(1150°C).
GBH5188 exhibits good ductility after prolonged exposure at
temperatures of 1200, 1400, and 1600°F (650, 760 and 870°C) for
16,000 hours.
Chemical composition
| Element | C | Cr | Ni | Co | W | Fe | B | La | Mn | Si | P | S | Cu |
| Weight(%) | 0.05~0.15 | 20.00~24.00 | 20.00~24.00 | Rem | 1300~16.00 | 3.00 max | 0.015 max | 0.030~0.120 | 1.25 max | 0.20~0.50 | 0.020 max | 0.015 max | 0.07 max |
Application
Because of its excellent strength, ductility and oxidation
resistance, GH5188 meets the critical high-temperature material
requiredments for gas turbine applications as well as many of those
in the airframe, chemical and nuclear fields. Typical uses are as
transition ducts, combustor cans, spray bars, flame-holders and
afterburner liners in jet engines.