White Aluminium Oxide Blasting Media Grits Al2O3 99% Purity High Cutting Efficiency
Brand Name:ZHENGTONG
Certification:ISO9001, ISO14001
Model Number:F12#-F220#
Minimum Order Quantity:1 MT
Delivery Time:8-30 days
Payment Terms:L/C, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Zhengzhou Henan
Address:
Ximazhuang, Liuzhai Town,Xinmi City, Zhengzhou, Henan, China
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
WHITE FUSED ALUMINA FOR SANDBLASTING
White aluminum oxide, also called White fused alumina , white
corundum etc., is electrically fused in arc furnace with high-grade
aluminum oxide powder as raw material, then made into different
grain size by crushing and reshaping, magnetic separation, and
screening. Compared with brown aluminum oxide, it is with higher
hardness and slight lower toughness. It also has features of high
purity, good self-sharpening, high cutting efficiency, less heat
emit, acid and alkali resistance, good thermal stability, etc..
Widely used for bonded and coated abrasive, polishing,
sandblasting, precision casting, refractory etc...
| Application | Specifications | The main chemical components% | |||||
| Al2O3 | Fe2O3 | SiO2 | Na2O | L.O.I | |||
Bonded Abrasives/ | F | F12-F80 | ≥99.3 | ≤0.10 | ≤0.05 | ≤0.35 | ≤0.2 |
| F90-F150 | ≥99.0 | ||||||
| F180-F240 | ≥99.0 | ||||||
| Coated Abrasives | P | 12#-80# | ≥99.3 | ≤0.10 | ≤0.05 | ≤0.35 | ≤0.2 |
| 100#-150# | ≥99.0 | ||||||
| 180-220# | ≥99.0 | ||||||
| Refractory | section | 0-1mm | ≥99.5 | <0.10 | <0.05 | <0.5 | <0.2 |
| 1-3mm | |||||||
| 3-5mm | |||||||
| 5-8mm | |||||||
| powder | 200-0 | ≥99.0 | <0.15 | <0.05 | <0.5 | <0.3 | |
| 325-0 | |||||||
| Color | Crystal Form | True Specific Gravity | Vickers Hardness | Mohs Harness |
| White | Trigonal Crystal | 3.95g/cm3 | 2200kg /mm2 | 9 |
FEATURES IN SANDBLASTING
The advantages of white aluminum oxide
1. High hardness, dense particles and good circularity of single
particles.
2. The color is pure white, no impurities, ensuring the color and
transparency of the wear layer.
3. The particle size distribution is evenly concentrated, the
single particle shape is consistent, and the minimum wear
resistance can be achieved with the minimum amount.
4. Chemical properties are stable and acid and alkali resistance , and the heat shrinkage is extremely small.
White Aluminum oxide blasting application | Abrasive grit Choose reference | |
| 1 | Aluminum alloy, zinc alloy workpiece blast cleaning to scratch,
squeeze lines, derusting, degreasing, descaling, etc., | 36#,100#,180#,220# |
| 2 | Copper, no need for bright light aftersanblasting: coating pretreatment, increasing surface adhesion. | 36#,200# |
| 3 | Steel material, pre-coated with plating to increase surface adhesion. Post-spray plating, painting, spray Teflon, spray aluminum, spray stainless steel, etc. | 30#,100# |
| 4 | Large steel parts are derusted, pre-treated before spraying, and rust-proof oil after sandblasting. | 24# |
| 5 | Steel and copper mold cleaning, removal of mechanical scratches, removal of surface residues and repair of molds. | 36#,100#,240# |
| 6 | Flat glass engraved or frosted, crystal crafts lettering. | 30#,150#,220#,320# |
| 7 | Plastic electronic original sanding, deburring, overflowing glue selection 180#-320# white corundum 180#,320# white corundum | 180#,320# |
| 8 | Glass products (matte crystal), glass, plastic lampshade sprayed into a matte effect. Use 100#, 180# WA 100#, 180# white corundum | 100#,180# |
| 9 | Plastic products remove light 120#,240# WA | 120#,240# |