Cold Drawn Annealed SAE J524 Seamless Hydraulic Tubing

SAE J524 cold drawn and annealed seamless low-carbon steel pressure tubing intended for use as
hydraulic lines and in other applications requiring tubing a quality suitable for flaring and bending.
The the cold drawn steel tubes mainly for hydraulic steel tubing and cold drawn pressure tubing

SCOPE
This specification covers cold drawn and annealed seamless low carbon steel pressure tubing for use as hydraulic lines.
HYDROSTATIC TEST
Tubing supplied under this specification shall have been tested at not less than 1,000 lbs. hydrostatic pressure or higher
in case working conditions require.
CLEANLINESS
It is desired that the inside of tubing shall be bright, clean, and free from grease, drawing compounds, oxide, scale,
carbon deposits, and any contamination that cannot be readily removed by cleaning with alkaline cleaners or benzine.
CORROSION PROTECTION OF INTERIOR OF TUBES
The inside of the tubing having open ends shall be protected by a coating of clean oil to protect the interior of the tubing against corrosion during shipment and normal storage periods.The corrosion preventive oil used shall be such that, after extended storage periods, it can readily be removed with an alkaline cleaning solution or with benzine (Standard Solvent).
QUALITY
Tubing shall be free from defects and in accordance with the best commercial practice.
CHEMICAL COMPOSITION (percentage by weight)
The tubing shall conform to the following chemical analysis:

Seamless low carbon steel tubing annealed for bending — Pressure type.
PHYSICAL PROPERTIES
The tubing shall conform to the following physical requirements
Tensile strength Lb/Sq. inch, minimum………………..45,000
Elongation in 2 inches, minimum………………………..35 percent*
For tubes with an OD of 3/8 inch and less and wall thickness of 0.035 inch and less, a minimum elongation of 30 percent is permitted.

A three inch section cut from the tubing shall not crack or show any flaws when flattened between parallel plates to three times the
wall thickness of the tube.
A section of tube approximately four inches in length with the ends burred shall withstand being expanded at one end over a polished
tapered mandrel having an included angle of 60 degrees until the actual average inside diameter is increased 30 percent.
The expansion test shall be made in a die in order to restrict the expansion of 30 percent. The axis of the mandrel should be paralled
to the axis of the tube during the expansion tests.
VARIATIONS
The diameter of the tubing shall not vary from that specified more than the following amounts:

Tags:seamless hydraulic tubing,SAE J524 seamless tubing,cold drawn hydraulic tubing,cold drawn
pressure tubing,SAE J524 steel tubing,Low-carbon steel tubes.Low carbon steel tubing,J524 round
tubing,J524 metal tubing.