Customized Polyamide Nylon Granules PA6 PA66 Pellets Reinforced 25% Firberglass
Brand Name:Polywell
Certification:SGS
Model Number:PA66GF25
Minimum Order Quantity:1 ton
Delivery Time:10-15 working days
Payment Terms:T/T, Western Union, MoneyGram
Contact Now
Add to Cart
Verified Supplier
Address:
Room2007, Building B, Huijin Business Center, Yangshe Town, Zhangjiagang City
Supplier`s last login times:
within 22 hours
Product Details
Company Profile
Product Details
Customized Polyamide Nylon Granules PA6 PA66 Pellets Reinforced 25% Firberglass
Introduction
- Our granules have good fluidity thus guaranteeing your smooth production. The good raw material can reduce the rate of rejects, and can produce high quality strips.
- Our PA66GF25 granules is special material for heat insulation profiles. It's extrusion grade modified plastics. It is different from PA66 resin.
- Our PA66GF25 granules is reinforced by 25% glass fiber.
Advantages
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.2%~1%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
Application
The PA66 granules with fiber glass are mainly used in thermal break strips, which are used in aluminum windows and doors.
Product Parameters
Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
Melting point | ºC | ≥240 | ≥240 |
Testing for tensile cracks | - | No cracks | No cracks |
Shore hardness | - | 80±5 | 80-85 |
Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
Elasticity modulus | MPa | ≥4500 | ≥4550 |
Elongation at break | % | ≥2.5 | ≥2.6 |
Tensile strength(transverse) | MPa | ≥70a | ≥70a |
High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
Water resistance tensile strength(transverse) | MPa |
| ≥35a |
Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Packing & Delivery
Packaging details: 25kg/bag
Delivery details: shipped in 10-15 working days after receiving the
payment
Customized Polyamide Nylon Granules PA6 PA66 Pellets Reinforced 25% Firberglass
Inquiry Cart
0