0.05mm CuNi23 Resistance Copper Nickel Alloy Price Wire
Brand Name:Tankii
Model Number:CuNi23
Minimum Order Quantity:15kg
Delivery Time:5-15days
Payment Terms:L/C, D/A, Western Union, MoneyGram
Place of Origin:China
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
1900 Mudanjiang Road, Baoshan District, 201999, Shanghai, China
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
Product Description
CuNi23 Resistance low temperature coefficient copper nickel binary
alloy for heating cable of automobile heating cushion
Introduction
CuNi23 resistance alloy is one of copper nickel binary alloys, having low temperature coefficient of resistance. It is applied to make rheostat, shunt, controller and other low voltage electrical components with a maximum operating temperature of 300°C. Due to its good heat coefficient, this alloy is widely used in low temperature heating cable of automobile heating cushion, railway snow melting, etc.
CuNi23Mn is very malleable and has a good resistance to corrosion until temperatures of 400°C. Ideal applications areas are all types of resistances used at low temperature.
CuNi23Mn is typically used in heating cables, fuses, resistors and various types of controllers.
Physical Data
Density 8.9 g/cm3
Specific Heat 0.37(J/kg 20°C)
Electrical Resistivity 0.03×10-6ohm.m
Melting Point 1150°C
Maximum Operating Temperature 400°C
Coefficient of linear expansion (coeff 10-6/°C) 15.7 from 20 to 1000°C
Typical Mechanical Properties
Mechanical Properties CuNi23
Tensile Strength 350 Mpa
Elongation 25%
Main Mechanical Properties:
Introduction
CuNi23 resistance alloy is one of copper nickel binary alloys, having low temperature coefficient of resistance. It is applied to make rheostat, shunt, controller and other low voltage electrical components with a maximum operating temperature of 300°C. Due to its good heat coefficient, this alloy is widely used in low temperature heating cable of automobile heating cushion, railway snow melting, etc.
Due to high tensile strength and increased resistivity values, the copper nickel alloy wires are the first choice for applications as resistance wires. With the different nickel amount in this product range, the characteristics of the wire can be chosen according to your requirements. Copper nickel alloy wires are available as bare wire, or enamelled wire with any insulation and self-bonding enamel. Furthermore, litz wire made of enamelled copper nickel alloy wire are available.
CuNi23Mn is a copper-nickel alloy (CuNi alloy) with medium resistivity for medium-low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F)
CuNi23Mn is very malleable and has a good resistance to corrosion until temperatures of 400°C. Ideal applications areas are all types of resistances used at low temperature.
CuNi23Mn is typically used in heating cables, fuses, resistors and various types of controllers.
Physical Data
Density 8.9 g/cm3
Specific Heat 0.37(J/kg 20°C)
Electrical Resistivity 0.03×10-6ohm.m
Melting Point 1150°C
Maximum Operating Temperature 400°C
Coefficient of linear expansion (coeff 10-6/°C) 15.7 from 20 to 1000°C
Typical Mechanical Properties
Mechanical Properties CuNi23
Tensile Strength 350 Mpa
Elongation 25%
Main Mechanical Properties:
| Cu | CuNi2 | CuNi6 | CuNi10 | CuNi23Mn | CuNi44 | ||
| Tensile strength | [N/mm²] | 220-300 | 260-360 | 270-370 | 300-390 | 500-550 | 560-680 |
| Yield strength at 1% elongation | [N/mm²] | 120-200 | 140-240 | 160-220 | 140-250 | 200-330 | 400-500 |
| Bending proof performance | [%] | 100 | 160 | 760 | |||
| Resistance (IACS) | [%] | 101 | 34 | 17 | 12 | 6 | 3 |
| Conductivity | [S*m/mm²] | 58.5 | 20.0 | 10.0 | 6.7 | 3.33 | 2.0 |
| Resistivity | [Ohm*mm²/m] | 0.0171 | 0.05 | 0.10 | 0.1493 | 0.30 | 0.50 |
| Thermal coefficient of resistance | [1E-6/K] | 3900-4300 | 1100-1600 | 500-900 | 350-400 | 150-200 | -80 - +40 |
| Solderability | [-] | good | good | good | good | good | no conventional soldering |
| main property type | Cuni1 | CuNI2 | CuNI6 | CuNi8 | CuNI10 | CuNi14 | CuNi19 | CuNi23 | CuNi30 | CuNi34 | CuNI44 | ||
| main chemical composition | Ni | 1 | 2 | 6 | 8 | 10 | 14.2 | 19 | 23 | 30 | 34 | 44 | |
| MN | / | / | / | / | / | 0.3 | 0.5 | 0.5 | 1.0 | 1.0 | 1.0 | ||
| CU | rest | rest | rest | rest | rest | rest | rest | rest | rest | rest | rest | ||
| max working temperature | / | 200 | 220 | 250 | 250 | 300 | 300 | 300 | 350 | 350 | 400 | ||
| density g/cm3 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | 8.9 | ||
| resistivity at 20 °c | 0.03 ± 10% | 0.05± 10% | 0.10± 10% | 0.12± 10% | 0.15± 10% | 0.20± 5% | 0.25± 5% | 0.30± 5% | 0.35± 5% | 0.40± 5% | 0.49± 5% | ||
| temperature coefficient of resistance | <100 | <120 | <60 | <57 | <50 | <38 | <25 | <16 | <10 | -0 | <-6 | ||
| tensile strength mpa | >210 | >220 | >250 | >270 | >290 | >310 | >340 | >350 | >400 | >400 | >420 | ||
| elongation | >25 | >25 | >25 | >25 | >25 | >25 | >25 | >25 | >25 | >25 | >25 | ||
| melting point °c | 1085 | 1090 | 1095 | 1097 | 1100 | 1115 | 1135 | 1150 | 1170 | 1180 | 1280 | ||
| coefficient of conductivity | 145 | 130 | 92 | 75 | 59 | 48 | 38 | 33 | 27 | 25 | 23 |