0.254 X 8.2mm ASTM B196 CuBe2 Copper Strips For Bearings

Brand Name:OHMALLOY
Certification:ISO 9001
Model Number:C17200
Minimum Order Quantity:20KGS
Delivery Time:10-20 working days
Payment Terms:T/T
Contact Now

Add to Cart

Verified Supplier
Location: Shanghai Shanghai China
Address: Room 311, No.1211, Mudanjiang Road, Baoshan district, Shanghai
Supplier`s last login times: within 1 hours
Product Details Company Profile
Product Details

0.254*8.2mm Astm B196 CuBe2 Copper Strips For Bearings


Product Normal Description:

Product Name: High strength and conductivity copper strips

Grade: CuBe2

Standard: ASTM B194, SAE J463, J461

Product Specification: 0.1mm-0.5mm

State: Annealed (A or TB00)

Typical Application: used for bearings


Chemical Composition of CuBe2 Copper Alloy:

Product Grade: UNS. C17200

Beryllium(Be): 1.80-2.00%

Cobalt(Co) + Nickel(Ni): 0.20% Min

Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max

Lead: 0.02% Max

Copper(Cu): Balance

Note: Copper plus additions equal 99.5% Minimum.


Typical Physical Properties of CuBe2 Copper Alloy:

Density (g/cm3):8.36
Density before age hardening (g/cm3):8.25
Elastic Modulus (kg/mm2 (103)):13.4
Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C):17 x 10-6
Thermal Conductivity (cal/(cm-s-°C)):0.25
Melting Range (°C):870-980

Temper Designations of CuBe2 Copper Strip:

UALLOYASTMMechanical and Electrical Properties of Copper Beryllium Strip
DesignationDescriptionTensile Strength
(Mpa)
Yield Strength 0.2% offsetElongation PercentHARDNESS
(HV)
HARDNESS
Rockwell
B or C Scale
Electrical Conductivity
(% IACS)
ATB00Solution Annealed410~530190~38035~60<13045~78HRB15~19
1/2 HTD02Half Hard580~690510~66012~30180~22088~96HRB15~19
HTD04Hard680~830620~8002~18220~24096~102HRB15~19
HMTM04

Mill hardened
930~1040750~9409~20270~32528~35HRC17~28
SHMTM051030~1110860~9709~18295~35031~37HRC17~28
XHMTM061060~1210930~11804~15300~36032~38HRC17~28

The Fabrication Properties of CuBe2 (C17200) Copper Alloys
Hot Working
  • C17200 copper alloys have good hot working capabilities.

Cold Working
  • C17200 copper alloys have excellent cold working properties.

Annealing
  • Annealing is the process of heating metal or glass and allowing it to cool slowly. This process removes internal stresses and strengthens it. C17200 copper alloys are annealed at temperatures from 774 to 802 degrees Celsius.

Other fabrication properties
  • Include blanking, drawing, drilling, forming and bending, tapping, and turning.