Annealed Metal Stainless Steel Plates 3mm Thick ASTM A240
Brand Name:TISCO,BAO STEEL MITTEL
Certification:SGS ISO MTC
Model Number:434 S43400 1.4113
Minimum Order Quantity:500KGS
Delivery Time:5 Days
Payment Terms:L/C, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Wuxi Jiangsu China
Address:
NO.288,YOUYI ROAD ,XI SHAN DISTRICT,WUXI CITY,CHINA
Supplier`s last login times:
within 48 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
1.4113 Steel Plate 3mm Thick ASTM A240 434 S43400 Stainless Steel Plate
RAW MATERIAL SPECIFICATIONS - Grade W-Nr 1.4113
MATERIAL CATEGORY: Common alloy steel - Ferritic corrosion
resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and
have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness
characteristics and weldability. Typically, these alloys are used
in aerospace applications, machinery and tooling and ordnance
components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1,
10297,10272,10312
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): -
Mo (％): 0.90 ~ 1.30
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): -
Mo (％): 0.90 ~ 1.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed - Thickness/mm: 100
Tensile strength, σb/MPa: 440~660
Yield strength, σ0.2≥/MPa: 280
Elongation, δ5 ≥(％): 18.0
Yield strength, σ0.2≥/MPa: 280
Elongation, δ5 ≥(％): 18.0
Reduction of area, ψ≥ (％): -
Impact, Akv≥/J: -
Hardness HBS30: 200min.
Impact, Akv≥/J: -
Hardness HBS30: 200min.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 750 ~ 850
air or water cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100:
250
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: 230
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: 230
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300:
210
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: 200
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: 200
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500:
-
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Annealed Metal Stainless Steel Plates 3mm Thick ASTM A240
Inquiry Cart
0