Name: SAE4340 GB 40CrNiMoA En 102503 Alloy Steel Rounds
Brand: Mittel
Price: 0.75 USD

China Categories

Home Products Suppliers Selling leads

English

Home /Products /Minerals & Metallurgy /Carbon Steel /Long Steel Products /

SAE4340 GB 40CrNiMoA En 10250-3 Alloy Steel Rounds

Brand Name:Mittel

Certification:SGS ISO MTC

Model Number:SAE4340 40CrNiMoA 36Crnimo4

Minimum Order Quantity:100KGS

Delivery Time:7 Working Days

Payment Terms:L/C, T/T

Contact Now

Add to Cart

JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Verified Supplier

Location: Wuxi Jiangsu China

Address: NO.288,YOUYI ROAD ,XI SHAN DISTRICT,WUXI CITY,CHINA

Supplier`s last login times: within 48 hours

View Contact Details

Product Details Company Profile

Product Details

36Crnimo4 Equivalent SAE4340 GB 40CrNiMoA En 10250-3 equivalent JIS SNCM439 Steel DIN 1.6511 Alloy Steel Bar

1.Supply Form & Size & Tolerance

Supply Form	Size(mm)	Process	Tolerance
Round	Φ6-Φ100	Cold Drawn	Bright/Black	Best H11
	Φ16-Φ350	Hot Rolled	Black	-0/+1mm
	Φ16-Φ350	Hot Rolled	Peeled/ground	Best H11
	Φ90-Φ1000	Hot Forged	Black	-0/+5mm
	Φ90-Φ1000	Hot Forged	Rough Turned	-0/+3mm
Flat/Square/Block	Thickness :120-800	Hot Forged	Black	-0/+8mm
Flat/Square/Block	Width:120-1500	Hot Forged	Rough Machined	-0/+3mm

Remark:Tolerance can be customized as per requests

2.Chemical Composition

Standard	Grade	C	Si	Mn	P	S	Cr	Ni	Mo
ASTM A29	4340	0.38-0.43	0.15-0.35	0.6-0.8	≤ 0.035	≤ 0.04	0.7-0.9	1.65-2.0	0.2-0.3
EN10250	36CrNiMo4	0.32-0.4	≤ 0.4	0.5-0.8	≤ 0.035	≤ 0.035	0.9-1.2	0.90-1.2	0.15-0.3
EN10250	1.6511	0.32-0.4	≤ 0.4	0.5-0.8	≤ 0.035	≤ 0.035	0.9-1.2	0.90-1.2	0.15-0.3
BS 970	EN24	0.36-0.44	0.1-0.4	0.45-0.7	≤ 0.035	≤ 0.04	1.0-1.4	1.3-1.7	0.2-0.35
BS 970	817M40	0.36-0.44	0.1-0.4	0.45-0.7	≤ 0.035	≤ 0.04	1.0-1.4	1.3-1.7	0.2-0.35
JIS G4103	SNCM439	0.36-0.43	0.15-0.35	0.6-0.9	≤ 0.03	≤ 0.03	0.6-1.0	1.6-2.0	0.15-0.3
GB 3077	40CrNiMoA	0.37-0.44	0.17-0.37	0.5-0.8	≤ 0.025	≤ 0.025	0.6-0.9	1.25-1.65	0.15-0.25

3.Physical Property

Density g/cm3	7.85
Melting point °C	1427
Poisson's ratio	0.27-0.30
Machinability (AISI 1212 as 100% machinability)	50%
Thermal expansion co-efficient µm/m°C	12.5
Thermal conductivity W/(m.K)	44.5
Modulus of elasticity 10^3 N/mm^2	210
Electric resistivity Ohm.mm2 /m	0.19
Specific heat capacity J/(kg.K)	460
Modulus of elasticity 10^3 N/mm2	100 ℃	200 ℃	300 ℃	400 ℃	500 ℃
Modulus of elasticity 10^3 N/mm2	205	195	185	175	165
Thermal expansion 10^6 m/(m.K)	100 ℃	200 ℃	300 ℃	400 ℃	500 ℃
Thermal expansion 10^6 m/(m.K)	11.1	12.1	12.9	13.5	13.9

4. Mechanical Property

Mechanical Condition	T	U	V	W	X	Y	Z
Ruling Section (mm)	150	100	63	30	30	30	30
Tensile Strength Mpa	850-1000	930-1080	1000-1150	1080-1230	1150-1300	1230-1380	>1550
Yield Strength,Mpa	≥665	≥740	≥835	≥925	≥1005	≥1080	≥1125
Elongation %	≥13	≥12	≥12	≥11	≥10	≥10	≥5
Izod Impact J	≥54	≥47	≥47	≥41	≥34	≥24	≥10
Charpy Impact J	≥50	≥42	≥42	≥35	≥28	≥20	≥9
Brinell Hardness HB	248-302	269-331	293-352	311-375	341-401	363-429	>444

5.High Temperature Strength

For quenched and tempered heavy forgings
Diameter mm	Yield strength MPa
Diameter mm	20 ℃	100 ℃	200 ℃	250 ℃	300 ℃	350℃	400℃
≤250	590	549	510	481	441	412	371
250-500	540	505	471	451	412	383	353
500-750	490	466	441	422	392	363	343

6.Forging

Forging temperature should be carried out between 1150℃-1200℃,The lower the forging-ending temperature ,the finer the grain size .hold suitable time for the steel to be thoroughly heated before forge, but don’t forge below minimum forging temperature 850°C. AISI 4340 has good forging characteristics,but crack is easily occured when improper cooling way after forged,so it should be cooled as slowly as possible in still air or in sand after forged.

7.Normalizing

Normalizing is used to refine the structure of forgings that might have cooled non-uniformly after forged,and considered as a conditioning treatment before final heat treatment.Normalizing temperature for AISI 4340 steel should be carried out between 850℃-880℃. hold suitable time for the steel to be thoroughly heated to complete the ferrite to austenite transformation.Cool in still air.

8.Annealing

Full annealing is recommended for AISI 4340 before machining, AISI 4340 should be carried our at a nominal temperature of 830℃-850℃,hold suitable time for the steel to be thoroughly heated, then furnace cooling to 610℃ at a rate of 11℃ per hour, finally air cooling.

9.Hardening

This heat treatment will obtain martensite structure after quenched.It will increase the surface hardness and strength.AISI 4340 should be carried out between 830℃-865℃, hold suitable time for the steel to be thoroughly heated, soak for 10-15 minutes per 25 mm section, oil quench is recommended.Tempering should be followed immediately after quenched.

10.Tempering

AISI 4340 alloy steel should be in the heat treated or normalized and heat treated condition before tempering.Tempering is usually carried out to relieve stresses from the hardening process, but primarily to obtain the required hardness and mechanical properties. The actual tempering temperature will be chosen to meet the required properties.it is usually carried out at 450℃- 660℃,hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm of section, and cool in still air.Tempering between 250℃-450℃ is not avoided as tempering within this range will seriously reduce the impact value,result in temper brittleness.

11.Application

AISI 4340 is often used in preference to AISI 4140 at the higher strength levels because of its better hardenability and improved CVN impact toughness.

Typical applications include:Heavy-duty axles, shafts, heavy-duty gears,spindles, pins, studs, collets, bolts, couplings,sprockets, pinions, torsion bars, connecting rods,crow bars, conveyor parts,forged hydraulic,forged steel crankshafts etc.

Company Profile

Jiangsu Mittel Steel Industrial Limited is located in Wuxi City, a beautiful city near Shanghai. Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest stainless steel sheet ,plate and coil supply Centers in China. Jiangsu Mittel Steel Industrial Limited was established in 1998 years. as one of the largest stockists and manufacturers of industrial grade Stainless Steel products and derivatives in Wuxi ,We keep a stock of 50000 tons every month, so we can delivery goods in fast time.

Our company supplies cold/hot-rolled stainless steel sheets,stainless steel coils and stainless steel Plate to many steel factories from athome and abroad, including Shanxi Taigang Iron& Steel CO, . Ltd (TISCO)Zhangjiagang Pohang (ZPSS), Shanghai BAO STEEL, Ningbo Baoxin and steel factories in Taiwan area, Mainland Chinese and foreign countries and regions.

Our long-term business lines are 201.202.304(1.4301).304L.316.316L(1.4404).430.409L, 309S ,310S(1.4845).317L.904L.S31803(1.4462).S32750.S32760, Finish: 2B, BA, NO. 1 NO. 4, HL, 8K and so on...Meanwhile, our company is also engaged in the long-term supply of homemade & imported medium and thick plates, galvanized and carbon steel products.

Adhering to the principle of "quality first and customer foremost",our company will offer long-term service to nationwide manufacturers of household appliances, elevators, tableware, ornaments, tanks and machines. We can offer precise frosted wiredrawing, 8K mirror finishing and skim board oil-abrasion of various specifications at any time. The precisely-processed products will meet your requirements for high quality. Our company is a modern enterprise integrating distribution and storage.

If you are interested in any of our products or would like to discuss a custom order, please feel free to contact us. We are looking forward to forming successful business relationships with new clients around the world in the near future.