42CrMo High Speed Forged Steel Rolls EN Standard Hot Roller Forging Hollow Bar
Brand Name:BAO STEEL MITTEL
Certification:SGS ISO MTC
Model Number:42crmo
Minimum Order Quantity:100KGS
Delivery Time:7 Working Days
Payment Terms:L/C, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Wuxi Jiangsu China
Address:
NO.288,YOUYI ROAD ,XI SHAN DISTRICT,WUXI CITY,CHINA
Supplier`s last login times:
within 48 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
42CrMo High Speed Forged Steel Rolls EN Standard Hot Roller Forging Hollow Bar
1. Supply Form of AISI 4140 Steel -ASTM A29/A29M Alloy Structural Steel
- Round
- Plate
- sheet
- Square
- Hexagonal
- Pipe
2. Supply Range of AISI 4140 Alloy Steel / 42CrMo4 steel
AISI 4140 Steel Round Bar: diameter 5mm – 400mm
ASTM 4140 Steel Plate: thickness 5 –500mm x width 200– 2300mm
SAE 4140 Steel Block: 210mm x 500-810mm
3. Chemical Composition of AISI 4140 Steel Material / 42CrMo4 steel
| ASTM A29/A29M | C | Si | Mn | P | S | Cr | Mo |
| 4140/G41400 | 0.35～0.40 | 0.20～0.35 | 0.70～0.90 | 0.025 Max | 0.025 Max | 0.80～1.10 | 0.18～0.25 |
| DIN 17220, EN 10083 | C | Si | Mn | P | S | Cr | Mo |
| 1.7225/42CrMo4 | 0.38～0.45 | ≤0.40 | 0.60～0.90 | 0.035 Max | 0.035 Max | 0.90～1.20 | 0.15～0.30 |
| GB/T 1229 | C | Si | Mn | P | S | Cr | Mo |
| 42CrMo | 0.38～0.45 | 0.17～0.37 | 0.50～0.80 | 0.030 Max | 0.030 Max | 0.90～1.20 | 0.15～0.25 |
| JIS G4105 | C | Si | Mn | P | S | Cr | Mo |
| SCM440 | 0.38～0.43 | 0.15～0.35 | 0.60～0.85 | 0.030 Max | 0.030 Max | 0.90～1.20 | 0.15～0.30 |
4. AISI 4140 alloy Steel Equivalent and Related Speciation / 42CrMo4 steel
| USA | German | Japan | China | ISO |
| ASTM 29/A29M | DIN 17350 | JIS G4404 | GB/T 1229 | ISO 683/18 |
| 4140 | 1.7225/42CrMo4 | SCM440 | 42CrMo | 42CrMo4 |
5. ASTM AISI 4140 Steel Material Mechanical Properties
Hardness, Rockwell C: 22 HRC, Density: 7.85kg/m3
Tensile strength: 655 MPa .
Melting point: 1416°C
Thermal expansion: 12.2 µm/m°C (20-100 ºC)
Elastic modulus: 190-210 GPa (at 25 ºC ).
6. Forging of AISI 4140 Oil and Gas industry Steel material metal
Forging of 4140 steel should be carried out between 2200 and 1650 º F (1200 and 900 º C). The lower the finishing temperature from forging, the finer will be the grain size. This alloy steel should ideally not be forged below 1650 º F (900 º C) and should be slow cooled after forging in Oil or water.
7. Heat Treatment of SAE/AISI 4140 Alloy Steel / 42CrMo4 steel
- 4140 Steel Annealing
Slowly heat to 800～8500 ºC, keep enough time, ensure heat thoroughly. then cooling in furnace to 480 ºC, then cool in air. After annealing, the hardness 92 HBS Max.
- AISI 4140 Steel Hardening & Quenching
4140 Steel is usually used at 18-22 HRc, If needs, AISI 4140 alloy steel can be hardened or Quenching by cold work. Quenching medium: oil
- Tempering Of AISI 4140 Alloy Steel
/ ℃ tempering temperature: 205 ~ 649°C.
After tempering hardness HRC: 18-25 HRc.
8. Application of AISI 4140 Alloy Steel / 42CrMo4 steel
AISI 4140 alloy steel used for Structural products. As below:
Oil and gas sector, like collets, connection rods, conveyor pins, stem assemblies, gears, Bearings
9. Quality Assured of AISI 4140 Alloy Steel / 42CrMo4 steel
Quality assured by Our ISO 9001:2008 quality management system. Our all AISI 4140 steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.
42CrMo High Speed Forged Steel Rolls EN Standard Hot Roller Forging Hollow Bar
Inquiry Cart
0