We supply V0 flame retardant TPEE resin:
1.Environment-friendly halogen containing fire grades of TPEE (FH
series)
Physical properties | Shore hardness | Tensile strength | Elongation at break | Tear strength | Melting point | Melt index | Brittle temperature | Density | Long-term working temperature | |
Unit | HD (3s) | MPa | % | KN·m-1 | ℃ | g/10min | ℃ | (g/cm3) | ℃ | |
Test methods | ISO868 | ISO527-1 | ISO527-1 | ISO34 | ISO3146 | ISO1133 | ISO974 | ISO1183 | ||
V-0Environment-friendly halogen containing fire-class | FH3303 | 35 | 16 | 460 | 85 | 178.6 | 7~12 | -60 | 1.32 | 120 |
FH2040 | 40 | 20 | 450 | 90 | 180.2 | 7~12 | -60 | 1.34 | 140 | |
FH4543 | 45 | 22 | 450 | 126 | 185.7 | 7~12 | -60 | 1.34 | 140 | |
FH5550 | 48 | 24 | 440 | 120 | 191.6 | 7~12 | -55 | 1.36 | 150 | |
FH605 | 55 | 26 | 440 | 123 | 194.2 | 7~12 | -50 | 1.36 | 150 | |
FH6555 | 58 | 29 | 420 | 143 | 194.6 | 7~12 | -50 | 138 | 150 | |
FH7560 | 63 | 32 | 400 | 147 | 203.4 | 7~12 | -50 | 1.38 | 150 | |
FH8570 | 70 | 32 | 380 | 190 | 208.6 | 7~12 | -50 | 1.38 | 150 | |
V-O high temperature resistance | FH60GE | 60 | 28 | 420 | 142 | 203.1 | 7~12 | -50 | 1.39 | 170 |
FH70GE | 70 | 32 | 380 | 198 | 210.3 | 7~12 | -50 | 1.39 | 180 |
Note:All the series have ROHS reports issued by SGS agency. When
the wire rod and so on toughness and fatigue resistance have higher
requirements, high temperature materials can partially substitute
Teflon as wire rod. The model can be used for injection molding,
extrusion molding process.
2.Low smoke halogen-free fire grades of TPEE (FK series)
Physical properties | Shore hardness | Tensile strength | Elongation at break | Tear strength | Melting point | Melt index | Brittle temperature | Density | Service temperature | |
Unit | HD(3s) | MPa | % | KN·m-1 | ℃ | g/10min | ℃ | (g/cm3) | ℃ | |
Test methods | ISO868 | ISO527-1 | ISO527-1 | ISO34 | ISO3146 | ISO1133 | ISO974 | ISO1183 | ||
V-0 Low smoke halogen-free fire-class | FK35 | 35 | 12 | 360 | 88 | 179.4 | 4~8 | -70 | 1.22 | 120 |
FK40 | 40 | 16 | 360 | 106 | 180.2 | 4~8 | -70 | 1.24 | 140 | |
FK48 | 48 | 18 | 350 | 120 | 192.5 | 4~8 | -60 | 1.30 | 150 | |
FK55 | 55 | 21 | 330 | 122 | 194.2 | 4~8 | -50 | 1.32 | 160 | |
FK58 | 58 | 23 | 330 | 143 | 196.3 | 4~8 | -50 | 1.32 | 170 | |
FK63 | 63 | 24 | 320 | 142 | 204.6 | 4~8 | -40 | 1.32 | 170 | |
FK68 | 68 | 26 | 310 | 184 | 210.5 | 4~8 | -40 | 1.34 | 180 |
he above data are typical.
The introduction of thermoplastic polyester elastomer SUNPRENE®TPEE Fire series:
The series have good fire resistance, toughness and high or low
temperature performance. It also retains the material itself, the
physical and chemical properties of stability, can meet a variety
of fire prevention purposes, including: electronic components,
cables, hoses, sheaths, etc.
The guideline of SUNPRENE®TPEE Fire series molding processing:
TPEE exhibits hydrolyzing resistance, then it doesn’t react with
water in the air. Because they have a little water absorption, we
must need to dry them before we process (although the moisture
content of TPEE is less than 0.1%, extrusion and molding process
will not have a defect.), for the workpieces perfect.
In acid medium, TPEE will degrade at high temperatures. Therefore,
TPEE and acid additives can’t be used simultaneously.
Before the molding process, TPEE must be dried under oven at
100~110 ℃ for 3~5h, and then processed immediately, not to let they
cooled and in damp air, or to affect their performance.
Processing technology:
1,Injection molding:barrel temperature should be higher than the
melting point of products 5~15 ℃, injecting pressure at 60~80 MPa,
mold temperature at 20~50 ℃, injecting speed in low speed.
2,Extruded into linear workpieces:when extruded into wire and other
workpieces, barrel temperature should be higher than the melting
point of products 5~10 ℃, recommended aspect ratio of 24:1, screw
speed in medium-low speed.