ASME SB677 TP904L / 1.4539 / UNS N08904 Stainless Steel Seamless Pipe
Brand Name:YUHONG
Certification:ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008
Model Number:ASME SB677 TP904L
Minimum Order Quantity:100KGS
Delivery Time:7DAYS
Payment Terms:L/C, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Ningbo Zhejiang China
Address:
20TH FLOOR,NO.1 NEW WORLD BUILDING ,NO.1018 MINAN ROAD,YINZHOU DISTRICT, NINGBO CITY, ZHEJIANG PROVINCE, CHINA
Supplier`s last login times:
within 3 hours
Product Details
Company Profile
Product Details
ASME SB677 TP904L/1.4539/UNS N08904 Stainless Steel Seamless Pipe
904L stainless steel material is a super austenitic stainless steel material, grade 00Cr20Ni25Mo4.5Cu, UNS: N08904, EN: 1.4539. It is a high alloyed austenitic stainless steel with low carbon content and has good corrosion resistance in dilute acid, designed specifically for environments with harsh corrosion conditions. It has a high chromium content and sufficient nickel content. The addition of copper gives it strong acid resistance, especially high resistance to chloride interstitial corrosion and stress corrosion cracking. It is highly resistant to corrosion spots and cracks, and has slightly better resistance to pitting compared to other steel grades. It has good machinability and weldability. Solid solution state without magnetism.
The chemical composition of 904L is C ≤ 0.03, Si ≤ 1.00, Mn ≤ 2.00, P ≤ 0.035, S ≤ 0.03, Ni: 23.0-25.0, Cr: 18.0-20.0, Mo: 3.0-4.0, Cu: 4.0-5.0. The minimum mechanical properties of 904L alloy at room temperature: alloy and state: 926, tensile strength (Rm N/mm2): 490, yield strength (RP0.2N/mm2): 216, elongation A5%: 35
Composition ranges for 904L grade of stainless steels.
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Cu | |
| 904L | min. max. | - 0.020 | - 2.00 | - 1.00 | - 0.045 | - 0.035 | 19.0 23.0 | 4.0 5.0 | 23.0 28.0 | 1.0 2.0 |
Mechanical properties of 904L grade stainless steels.
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) | Brinell (HB) | ||||
| 904L | 490 | 220 | 35 | 70-90 typical | - |
| Rockwell Hardness value range is typical only; other values are specified limits. | |||||
Typical physical properties for 904L grade stainless steels.
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Co-eff of Thermal Expansion (m/m/C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100C (J/kg.K) | Elec Resistivity (n.m) | |||
| 0-100C | 0-315C | 0-538C | At 20C | At 500C | |||||
| 904L | 8000 | 200 | 15 | - | - | 13 | - | 500 | 850 |
Grade specifications for 904L grade stainless steels.
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| 904L | N08904 | 904S13 | - | 1.4539 | X1NiCrMoCuN25-20-5 | 2562 | - |
| These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted. | |||||||
Possible alternative grades to 904L stainless steel.
| Grade | Why it might be chosen instead of 904L |
| 316L | A lower cost alternative, but with much lower corrosion resistance. |
| 6Mo | A higher resistance to pitting and crevice corrosion resistance is needed. |
| 2205 | A very similar corrosion resistance, with the 2205 having higher mechanical strength, and at a lower cost to 904L. (2205 not suitable for temperatures above 300C.) |
| Super duplex | Higher corrosion resistance is needed, together with a higher strength than 904L. |
ASME SB677 TP904L / 1.4539 / UNS N08904 Stainless Steel Seamless Pipe