Hot Rolled 304 Stainless Steel Plate 3.0 - 16.0mm SS Plate EN 10088 1.4319 Stainless Steel
Product Name | 301 stainless steel plate |
Standard | ASTM, EN |
Brand | TISCO |
Certificate | MTC according to EN 10204-3.1 |
Specification | Cold rolled sheet Thickness: 0.4 - 2.5mm Size:1219x2438mm |
Hot Rolled plate: Thickness: 3.0 - 16.0mm Size: 1500 x 6000mm | |
Surface | Hot Rolled: No.1 |
Cold Rolled: 2B, | |
Trade terms | Ex-Work, FOB/CFR/CIF |
Payment terms | T/T, L/C at sight, Western Union,etc. |
Delivery Time | 5-8 days after receive the deposit. |
Packing | Water proof film coated, standard export package or as required. |
Port of shipment | 201, 202, 301, 302, 304, 304L, 316, 316L, 310S, 310,405, 409, 430, 410, 420, 440A,904l, etc |
Stainless steel grade 301 is usually supplied in the form of strips and wires, with a tensile strength of up to 1800 Mpa, to produce tempers ranging from 1/16 Hard to Full Hard. By subjecting grade 301 to controlled analysis it is capable of retaining sufficient ductility even in ½ hard conditions. This form of grade 301 may be used in aircraft, rail car components and architectural structures. Tempers of this grade, ranging from ¾ to full hard, may be used in applications requiring high wear resistance and spring features with simple form designs.
Grade 301L, which is the low carbon form of grade 301, is the ideal choice for applications that require good ductility. Grade 301LN is another variant. This contains a higher percentage of nitrogen and exhibits a higher work harden rate compared to standard 301. Only grade 301 is specified in ASTM A666. 301L and 301LN are represented by other conventions. Grade 301L is represented by JIS G4305 and 301LN by EN10088-2 as grade 1.4318.
Composition ranges of stainless steel grade 301 are tabulated below.
Table 1 - Composition ranges for 301 grade stainless steel
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
301 ASTM A666 | min. max. | - 0.15 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0 18.0 | - | 6.0 8.0 | - 0.10 |
301L JIS G4305 | min. max. | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0 18.0 | - | 6.0 8.0 | - 0.20 |
1.4318/301LN EN 10088-2 | min. max. | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.015 | 16.5 18.5 | - | 6.0 8.0 | 0.10 0.20 |
The mechanical properties of grade 301 stainless steels are listed in the table below. The bend test is obtained around a diameter of the bend factor multiplied by the steel thickness.
Table 2 - Mechanical properties of 301 grade stainless steel
Grade 301 Temper ASTM A666 | Tensile Strength (MPa) min. | Yield Strength 0.2% Proof (MPa) min. | Elongation (% in 50mm) (thick.>0.76mm) min. | Bend Test (thickness > 1.27mm) | |
Bend Angle (°) | Factor | ||||
Annealed | 758 | 276 | 60 | - | - |
1/16 Hard | 620 | 310 | 40 | 180 | 1 |
1/8 Hard | 690 | 380 | 40 | 180 | 1 |
1/4 Hard | 862 | 514 | 25 | 90 | 2 |
1/2 Hard | 1034 | 758 | 18 | 90 | 2 |
3/4 Hard | 1205 | 930 | 12 | 90 | 3 |
Full Hard | 1276 | 965 | 9 | 90 | 5 |
Some of the typical applications of grade 301 stainless steels are listed below: