Electrophoretic ED Paint Good Coating Fullness For Locomotive Industry
Brand Name:HAOLISEN
Certification:IATF16949 , ISO9001
Model Number:HR-4000BLB/HR-6000
Minimum Order Quantity:Negotiation
Delivery Time:30-60 Days
Place of Origin:Shanghai China （Mainland）
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
15/F, No.1185, Huyi Road, Jiading District, Shanghai，China.
Supplier`s last login times:
within 1 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details
Company Profile
Product Details
Electrophoretic coating for locomotive industry
Product Introduction
HR-4000BLB/HR-6000 the bottom of one black cathode electrophoretic coating, is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating, such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.
This product features shown below:
| The appearance of the coating is flat, delicate, smooth. |
| Good stability of bath can adaptable for a longer updating cycle. |
| Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting |
Main ingredients
| Matrix resin: | Acrylic modified epoxy resin |
| Curing agent | Fully enclosed multi isocyanate |
| Additives | surface active agent, prevent shrinkage cavity agent |
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HR-4000LB) | Black Paste (HR-6000) | |||
| Conductivity | 25℃, μs/cm | 1000±500 | —— | HG/T 3334 |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Bath on site management project
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:(6-8) | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 15±5 | -- | once a day | |
| PH | 5.4-6.0 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1000±500 | 1400±900 | once a day | |
| P/B | 0.08-0.15 | once a week | ||
| L panel | Smooth horizontal plane and vertical plane without obvious differences | once a week | ||
| Solvent content (%) | 0.5-1.8 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥350 | once a week | ||
| Bath temperature ( ℃ ) | 28-35 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-190 | once a day | |
| Curing conditions | Drying temperature | (165-185)℃×(20-30)min (With content holding time) | once a day | |
Electrophoretic ED Paint Good Coating Fullness For Locomotive Industry