High Pressure Drilling Mud Pumps Ceramic Liner drilling rig tools
Description:
- HYRD Petroleum Technology Co., Ltd. ,which has passed ISO9001 Authentication, specializes to research, develop and manufacture the Mud Pump and its expendable parts and its technology & quality control are in line with API Spec 7K Standard.
The Products can be supplied:
Liner
Liner is divided into Ceramic Sleeve Liner, Double Metal Liner, Carburization & quenching Liner and Chrome-plated Liner
a.) Ceramic Sleeve Liner
Material of sleeve is Zirconia and its shell is 45#(ASTM1045)forged steel.
1 . Mud Pump:
8P-80,9P-100,10P-130,12P-160,F-500,F-800,F-1000,F-1300,F-1600,PZ-7,PZ-9,PAH,TEE,W-440,W-446,3NB350,3NB-500C,3NB-800C,3NB-1000C,3NB-1300C,3NB-1600
2. Plunger Pump:
TWS600S,TWS2000,DOWILL300,HyT-400.
3. Skid- mounted & Pump Unit for each kinds of pump said above.
4. Spare Parts and Expendable parts: With the specialized & batched production liner, we can supply power end assembly, fluid end assembly and its spare parts, which can be easily matched & exchanged with some international famous mud pump brand.
Lake Petro has best processing & test equipments, which can undertake maintenance & repair services for each kind of mud pump.
Lake Petro has its own import & export License and formed its unique style sale network & service image and the products have been sold to United States, Mexico, Canada, British, German, Egypt, Nigeria, Russian, UAE etc.
No | Properties | Units | Values | Remark |
1 | Composition | % | Y2O3+ZrO2≥99.5% | ZrO2≥95% |
2 | Density | g/cm³ | 5.95-6.05 | |
3 | Flexural Strength | Mpa | 800-1200 | |
4 | Tensile Strength | Mpa | 500-600 | |
5 | Weibull Modulus | M | >30 | |
6 | Compressive Strength | Mpa | >1950 | |
7 | Modulus of Elasticity | Gpa | 200 | |
8 | Poisson `s Ratio | 0.31 | ||
9 | Hardness | HV0.3kg/mm² | >1120 | HB≥87 |
10 | Fracture Toughness | Mpam¹/² | 8-10 | |
11 | Average Grain Size | μm | 0.4-0.6 | |
12 | Thermal Conductivity | W/m*K | 3.08 |
b). Double Metal Liner
Material for shell is forged steel pipe or seamless steel tube, 45#(ASTM1045). Normalizing hardness degree is 160BHN(HB180-200), percentage elongation 17%(δ>17%),tensile strength not less than 85000PSI(σb>610Mpa), Flexural Strength not less than 60000PSI(σb>450MPa)and shell with HP.
Sleeve material is high chrome centrifugal, which is chrome containing 26-28%, its thickness 0.25~0.35 inch (6.35 -8.89mm. its standard thickness is 7mm and special thickness reduced has 3 kinds, 4mm, 4.5mm & 5mm. Normally, it means standard thickness if there is no special explanation ), quenching hardness HRC59-67.
Its Chemical Composition Table is as following
Element | C | Cr | Si | Mn | Mo | S,P |
Content | 2.8%-3.1% | 26%-28% | 0.6%-0.9% | 0.5%-1% | 0.5%-0.8% | <0.05% |
Some special chemical composition will be adopted to use on the sleeve according to the requirement of the client or special working conditions
c). High Frequency, Carburization & quenching Liner Material is 20#(ASTM1020)seamless steel tube or forged steel. The bore will be carburized first and then High Frequency quenching . The thickness of Carburized layer is more than 1.5mm and hardness of the bore is HRC58-62
d). Chrome-plated Liner
Material is 45#(ASTM1045)or 40Cr(ASTM5140)seamless steel tube or forged steel. Thickness of chrome plated is 0.15~0.2mm and hardness of Carburized layer is more than 1.5mm and hardness of the bore is HRC58-62