Hollow Co-extrusion WPC Composite Decking Tiles Rotproof for Garden

Hollow Co-extrusion WPC Composite Decking Tiles Rotproof for Garden

Brand Name:Huaxiajie
Certification:ISO9001:2000, Soncap, Intertek, SGS
Model Number:WPC Decking-13
Minimum Order Quantity:500 m²
Delivery Time:15days/20’ container, 25days/40’ container
Payment Terms:30% TT as the deposit, the balance before delivery
Contact Now

Add to Cart

Verified Supplier
Address: NO 355 Zhiyuan Road ,Wukang Town, Deqing County, Zhejiang Province, China
Supplier`s last login times: within 24 hours
Shipping
lt's easy to get a shipping quote! Just click the button below and complete the short form.
Get Shipping Quote
Product Details Company Profile
Product Details

Hollow Co-extrusion WPC Composite Decking Tiles Rotproof for Garden


Description:


Characteristic of Composite Rotproof Decking Tiles:


1Green material,recyclable
2

Easy to maintain and install

3

Durable - moistureproof and antislip

4

Stronger and more Flexible

5

Standard wood working tools can be used

6

UV-resist and color stability

7

Dimension stability against moisture and temperature.suitable from -40 to 60

8

Weather resistant, suitable from -40 to 60

9

Green ecological, Innovative technology, Lifestyle

10

Elegant nature wood grain texture and touch, with wood scent

11

Elegant and detailed shape design


All the standard embossing is available with this option.

It offers the best combination of price and quality.

Different surface treatment options are available as added features.

The unique embossing patterns enhance the beauty of the boards,

as well as adding to its authenticity.

Beauty/Strong/Dependable.


Specifications:


Name

Hollow Co-extrusion WPC Composite Decking Tiles Rotproof for Garden

Size

140*25mm

Length

1-6m,Customized

Color

Teak, Beech, Black Walnut, Coffee, Customized color

Material component

60% PVC+30% Wood Powder+10% special additives

Surface

Smooth, Brushed, Scratched, Grain optional

Warranty

15years

Certificate

ISO9001, ISO14001, CE, SGS

Lifetime

25years

Package

pallet with PVC soft flim

Range of use

Garden, Lawn, Balcony, Corridor, Garage, Pool&SPA Surrounds, Boardwalk,

Playground


Zhejiang Huaxiajie Macromolecule Building Material Co., Ltd., which was established in 2004, is a special manufacturer of PVC wall and Composite Rotproof Decking Tiles, PVC doors and doorframes, and plastic-wood skirting and flooring. Our products are environment friendly.
With advanced production lines from Germany and Italy, we have a total annual capacity of over 5 million square meters PVC wall and ceiling panels, over 6,000MT plastic-wood products, and over 2,000MT other PVC products.


Test Reprot:


Table 2.Test Results

Test Method

Characters

Result

ASTM G155

Weathering Resistance

After 2000hours weathering test

Grey scale:3

There was some color changer on the

surface.


Table 2

Test Method

Characters

Result

ASTM D 256

Impact resistance

59.1 J/m

Break type Complete break

ASTM D 790

Flexural strength

(Thickness:3mm,span:48mm)

MOR::79.8Mpa

MOE:3107Mpa

ASTM D1037

Water absorption and

Swelling in thickness

(24hours immersion)

Water absorption:0.16%

Swelling thickness:0.10%

ASTM D2395

Specific gravity

1.17g/cm3

ASTM D4060

Abrasion Resistance

(CS-17,2000cycles)

Weight Loss:0.12g

ASTM D696

Coefficient of linear

thermal expansion

(-30℃~30℃)

5.13*10-5 1/℃

ASTM D2394

Slip Resistance Test


Static Slip Resistance

Dynamic Slip

Resistance

Dry surface

0.63

0.45

Wet Surface

0.69

0.68

ASTM D638

Tensile strength

37.2MPa

ASTM

D7032and

ASTM

D6109

Flexural strength:Initial

(Thickness:27mm,span 432mm)

MOR:33.2Mpa

MOE:2073Mpa

Flexural strength Temperature

and moisture effects(-29℃ for 7days)

MOR:35.0Mpa,increase 5.4%

MOE:2209Mpa, increase 6.6%

Flexural strength Temperature and

moisture effects(52℃ for 7days)

MOR:35.2Mpa,increase 6.0%

MOE:2162Mpa, increase 4.3%

Flexural strength Temperature

and moisture effects(immersing

in water for 7days)

MOR:33.4Mpa,increase 0.6%

MOE:2103Mpa, increase 1.4%

ASTM D7031

and ASTM

D6109

Flexural strength

(Thickness:27mm,span:432mm)

(After freeze-thaw resistance)

MOR:33.4Mpa,increase 6.0%

MOE:2167Mpa, increase 4.5%

ASTM D1761

Fastener withdrawal test

2387.8N




China Hollow Co-extrusion WPC Composite Decking Tiles Rotproof for Garden supplier